industrial High strength Magnesia Chrome Bricks Fire Resistant bricks

Delivery Time:20-30DAYS
Certification:ISO9001

Quick Detail:

♦ High strength

♦ Corrosion resistance

♦ Erosion resistance

♦ Excellent slag resistance

♦ Good thermal shock stability

Description:

It is made with sintered magnesia and refractory level chrome ore as raw materials. The space between refractory grains is bonded with silicate. The domestic so called magnesia –Chrome bricks .

The refractoriness of magnesia chrome bricks are more than 2000℃,and the refractory under load is a above 1550℃.Good steady volume in high temperature , the performance of meeting sudden cold and sudden hot is better than magnesia bricks

Specifications:

Direct-Bonded Magnesia-Chrome Brick

Main Application:It’s mainly applied to line the sintering zone of the new dry-processing of cement kilns and glass tank furnaces as checkers and the other industrial furnaces.

Chemical & Physical Data

Brand	MgO %	Cr2O3 %	SiO2 %	A.P. %	BDg/cm3	CCS.MPa	R.U.L ℃
DBMGe-8A	≥74	≥8	≤1.5	≤18	2.98	≥40	1660
DBMGe-8B	≥74	≥8	≤2.0	≤18	2.98	≥35	1600
DBMGe-12A	≥66	≥12	≤1.5	≤18	3.1	≥40	1660
DBMGe-12B	≥66	≥12	≤2.0	≤18	3.1	≥35	1600
DBMGe-16A	≥60	≥16	≤1.5	≤18	3.15	≥40	1660
DBMGe-16B	≥60	≥16	≤2.0	≤18	3.15	≥35	1600

Rebonded Magnesia-Chrome Brick

Main Application:It’s suitable for lining of the slag zone area of refining furnaces of VOD,SKF.

Chemical & Physical Data

Brand	MgO %	Cr2O3 %	SiO2 %	A.P. %	BDg/cm3	CCS.MPa	R.U.L ℃
RBMG-16A	≥65	≥16	≤1.2	≤16	3.1	≥45	1750
RBMG-16B	≥60	≥16	≤1.6	≤16	3.1	≥40	1700
RBMG-20A	≥60	≥20	≤1.2	≤16	3.15	≥45	1750
RBMG-20B	≥60	≥20	≤1.2	≤16	3.15	≥40	1700

Semi-Rebonded Magnesia-Chrome Brick

Main Application:It’s widely used for every industrial