ER70S-6 copper coated/sg2/g3si1 welding wire

 bronze mig welding wire ER70S-6                                     

AWS A5.18 ER70S-6 ;  GB ER50S-6 ; JIS YGW12 ; DIN 8559 SG2 ; 
 EN 440 ISO 14341-A    G 46 4 M G3Si1 / G4Si1

2.Application of 0.8mm ER70S-6 welding wire/mig mag welding wire  :  

Welding of carbon steel , low alloy steel & 500MPa grade low alloy high intensity steel structures etc.such as vehicle , building ; bridge , ship-building , pressure vessel industry , pipeline etc.

3.Advantages of 0.8mm ER70S-6 welding wire/mig mag welding wire  :  

1.  Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.

2. High current-resistance

3. High iron rust resistance

4. Small stomatal sensitivity

5.  Little deformation after welding.

6.  Wide applicability. Suitable for welding thin, medium and thick plates. 

Standard:AWS: ER70S-6/DIN SG2/BS A5.18/JIS YGM12, LY ER50-6, GB/T: ER50-6

Wire diameter: 0.8 /0.9/ 1.0 / 1.2 / 1.6 mm
Coil diameter: 220/270 /300mm
Weight: 1/5/15 kg
Winding: inline-layered, dense
Packing: wire on plastic reels in shrink film and a cardboard box

Surface treatment:copper( Chemical coating of copper, advanced processing technology) 

Sheilding Gas:fully CO2 ; 75%-95% Ar + rest of CO2 ; 95% Ar + rest of CO2 

Welding Process: Gas Metal Arc Welding -- GMAW / MIG Welding Process