E316L-16 stainless steel welding electrode

Specifications

Stainless steel welding electrode E316L-16 USD3.00-3.80/KG,exported Australia,Brazil,Singapore,Spain,Russia,Ukraine,USA etc

Stainless steel welding electrode E316L-16 is a titanium calcium type coating of the pressure vessel steel special low carbon stainless steel electrode, the weld metal carbon content ≤ 0.04%, with good heat resistance, corrosion resistance and crack resistance. Can be AC and DC. Good welding performance.
Uses: used for synthetic urea and equipment for welding stainless steel pressure vessels.

Deposited metal chemical composition (%)

C	Mn	Si	Cr	Ni	Mo	Cu	S	P
≤0.04	0.5~2.5	≤0.90	17.0~20.0	11.0~14.0	2.0~3.0	≤0.75	≤0.030	≤0.035

Mechanical Properties of Deposited Metal

σb(MPa)	δ5(%)
≥490	≥30

X RADIOGRAPHIC EXAMINATION REQUESTED: I-LEVEL

Reference current

Electrode diameter(mm)		2.0	2.5	3.2	4.0	5.0
Welding current (A)	Flat welding	30~50	60~85	85~120	115~160	160~200
	Vertical welding	30~50	50~70	75~105	95~130

Notes

1, welding electrodes shall be 150 °C baking 1 hour.
2, welding DC power supply as far as possible, because the AC welding penetration shallower. Current is not too large, so that Welding Rod red.
3, welded parts must be removed before welding oil, rust, water and other impurities.
4, corrosion resistance of deposited metal test determined by the agreement between supply and demand.