soft magnetic materials,Amorphous Ribbon, Iron Core 1k 107

Saturation magnetization(Bs)

1.25T

Saturation magnetostrictive coefficient(λs)

<2×10-6

Curie temperature(Tc)

560℃

Density(d)

7.3g/cm3

Crystallization temperature(Tx)

510℃

Resistivity(ρ)

130μΩ-cm

Hardness(Hv)

800

Continuous operating temperature range

-55~130℃

Annealing method

Non-magnetic annealing

Initial permeability

>150,000

Maximum permeability

>600,000

Residual magnetic flux density

0.6T

Coercivity

<0.8A/m

Iron loss P(20kHz,0.5T)

<25W/kg

Iron loss P(100kHz,0.3T)

<150W/kg

Iron loss change rate (-55℃~125℃)

<15%

Width(mm)

Thickness(μm)

5

30±2

10

30±2

15

30±2

20

30±2

30

30±2

Other columns dimensions available according to requirements. (5~50mm)