Hot Selling Photovoltaic Solar Panel High Quality EVA Film

Name: Hot Selling Photovoltaic Solar Panel High Quality EVA Film
Brand: REOO
SKU: 112094377
Availability: InStock

US$ 1.38 - 1.42 MOQ: 10 Square Meters

Key Specifications

Place of Origin:

Jiangsu, China

Brand Name:

REOO

Model Number:

JCC-105

Nantong Reoo Technology Co., Ltd.

Payment & Shipping

Payment Methods:

Port of Shipment:

Shanghai

Delivery Detail:

Delivery time depends on order quantity.

Place of Origin Jiangsu, China

Brand Name REOO

Model Number JCC-105

Type Other

EVA Film for solar panel manufacturing

Overview

EVA film characters:

Related Parameters

Size:

Storage and life time:

1,T≤30°C,H≤70%
2,Shift time is 6 monthes
3,All open carton EVA film must be used up within 24hours and avoid it absorb some dust and water

Environment:

NO	Project	Technical index	Unit	Note
1	Storage temperature	0-30	℃	Too high temperature can cause gum surface adhesion even accepting the cross linking
2	Storage humidity	Storage temperature	%	Poor save may cause it full of moisture to produce bubble
3	Storage condition	keep in dark place	/	ray of light may cause the additives lose efficacy and even make it yellow
4	Storage Conditions	Away from the heating equipment, dust, oil pollution; fire		Cause the change of the products’ quantity
5	Open deadline	no more than 6 months		Suggest finish it before 48 hours
6	service life	Have the relevant international certification Suggest for 25 years	Year	Have passed the high temperature, high humidity, 1000 h test

Main performance parameter of product curing:

Product type		Fast Cure	High penetration
Project	Unit	JCC-105	JCC-105-T
Melt index (before curing, 190℃)	g/10min	30±2	30±2
Softening point (before curing)	℃	59±1	59±1
Density	g/cm³	0.96	0.96
specific heat	J/℃,g	2.45	2.45
strength of extension	Mpa	24	24
ductility	%	450	450
light transmittance (after curing)	%	>91.0	>91.5
Absorptivity (20℃,24h)	%	<0.1	<0.1
Insulation resistance	MΩ	1.45*106	1.45*106
puncture voltage	Kv/mm	19	19
percentage of contraction (test before curing test before, 120℃, 5min)	%	MD<3.5	MD<3.5
	%	TD <1.0	TD <1.0
Completely cross linking degree (140℃, 15min)	%	>80.00	>80.00
Peel strength of film with glass (140℃,15min after curing)	N/cm	>80	>80
Film and TPT peel strength (140℃, 15min after curing)	N/cm	>60	>60
Ultraviolet aging resistance (UV,1000hr)	%	>90	>88
High and low temperature wet and heat aging	%	>88	>88