Galvanized Iron Wire ( Factory) Low Carbon Steel Galvanized Wire

Production Standard:ASTM B498:GB/T 3428

Raw Material:High quality low carbon steel wire.

Wire Diameter:1.25mm-5.5mm

Zinc Coating:45g-300g/m²

Tensile Strength^:900-2200g/m²

Feature:High Tensile Strength,Good Elongation and Yiled Strength

Production Process

It is made of high-quality low-carbon steel wire rod and is made of high-quality low-carbon steel, which is processed by drawing, pickling and rust removal, high temperature annealing, hot-dip galvanizing and cooling.

characteristic

The galvanized iron wire has good toughness and elasticity, and the maximum amount of zinc can reach 300 g/m2. It has the characteristics of thick galvanized layer and strong corrosion resistance.

application

Products are widely used in construction, handicrafts, wire mesh, highway fences, product packaging and daily civil use.

The wire for building bundling is 22# (0.71mm), the price is low, its characteristics are flexible and not easy to break. It is one of the most ideal wire binding in the construction industry, mainly using low-zinc cold-plated wire. Mainly used as low-zinc cold-plated iron wire.

Handicraft iron wire, using a special processing of a line, no broken ends, the amount of zinc on the uniform and bright, the general price is slightly more expensive.

The galvanized wire also includes the sprinkling line: the weight of each plate is about 100 kg-1000 kg per roll, which is mainly suitable for industrial, agricultural and animal husbandry.

The galvanized wire is divided into hot-dip galvanized wire and cold-galvanized wire (electro-galvanized wire).

Technical Parameters:

Tensile Strength (Mpa)

The tensile strength is defined as the maximum load achieved in the tensile test, divided by the cross-sectional area of the wire test piece. Galvanized Wire is produced using soft, medium and hard grade wires. The following table specifies the tensile range according to the grade: