Polyurethane Synthetic Perforated Leather Fabric Full Five Color Eco Bonded Leather

Delivery Time:15 days after received the deposit

Polyurethane Synthetic Perforated Leather Fabric Full Five Color Eco Bonded Leather

Tearing strength

Weft: >10lbf/3cm Longitude: >12lbf/3cm

Peeling strength

Weft: >3kg/3cm Longitude: > 3kg/3cm

Elongation

Weft: >15% Longitude: > 10%

Anti-hydrolysis(shelf life)

At least 5 years

Color fastness to light

> BWS 5

Cold crack of finishing

No cracking -30℃

Fire Retardant

BS5852 CA117 FAR25.853 CFR1633 FMVSS-302

Color fastness to Rubbing

(Change of leather color)

Dry: >500 cycles GSR 4

Wet:>250 cycles, GSR 4 Perspiration:>80cycles GSR4

This production is suit for sofa, chair and so on. which is very like real leather backing.

The thickness: 1.0mm to 1.2mm

It is conformed with standard of EURO market.

The abrasion resistant: more than 50000 times.

The Width: 54\"

Test	Method	Requirement	Results	Pass/Fail
Azo dyetuffs (Arylamines)	BLC7C.1based on BS EN ISO 17234-1:2010	Not detectable (detection limit:30mg/kg)	None detected (<30mg/kg)	Pass
Chromium VI,soluble	BS EN ISO 17075:2007	Not detectable (detection limit:3.0mg/kg)	None detected (<3.0mg/kg)	Pass
Formaldehyde	BLC 7A.9 based on BS EN ISO 17226-1:2008	General <75mg/kg	54mg/kg	Pass
Chlorinated phenols PCP,TCP&TeCP	BLC 7B.5 based on BS EN ISO 17070:2006	Not detectable (detection limit:1.0mg/kg)	None detected (1.0mg/kg)	Pass
PH	BS EN ISO 4045:2008	Min.3.2.if the pH value is below 4 or above 10,the diff.figure shall be <0.7	PH=6.19	Pass
Extractable heavy metals screening	BS EN 71-3:1995 Migration of elements	Pass as specified in BS EN 71-3:1995	See separate table for indivi -ual result	Pass
Dimethyl fumarate (DMF)	BLC 7A.6 GC-MS analysis	None Detectable <0.1mg/kg	None detected (0.1mg/kg)	Pass