C11000 Electrolytic Tough Pitch Rods for Railways Engine Components

 

Spec Equivalents: CDA 110 ETP, ASTM B124, ASTM B152, ASTM B187, ASTM B188, ASTM B272

The electrolytic tough pitch copper is the copper with high thermal and electrical conductivity. The products manufactured using this copper possess good corrosion resistance and soldering ability. The inherited fabrication qualities of the copper allows it to bend, drilled, soldered, riveted and to be fit in to almost any design specifications. This variant of copper has excellent hot workability.

Applications:

• Electrical Industry
• Telecommunications Industry
• Architectural Industry
• Antimicrobial Applications

Equivelent Specifications:

End Product	Specification
Bands, Projectile Rotating	MILITARY MIL-B-20292
Bar	ASME SB133, ASTM B152, SAE J461, J463
Bar, Bus	ASTM B187
Bar, Forging	ASTM B124
Bolts	ASTM F468
Brazing Filler Metal	FEDERAL QQ-B-650
Foil, Printed Circuits	ASTM B451
For, Forging	ASTM B124
Forgings, Die	ASTM B283
Nuts	ASTM F467
Pipe, Bus	ASTM B188
Plate	AMS 4500, ASTM B152, SAE J461, J463
Rod	ASME SB133, MILITARY MIL-C-12166, SAE J461, J463
Rod, Bus	ASTM B187
Screws	ASTM F468
Shapes	SAE J461, J463
Shapes, Bus	ASTM B187
Shapes, Forging	ASTM B124
Sheet	AMS 4500, ASTM B152, B694, SAE J463, J461
Sheet, Building Construction	ASTM B370
Sheet, Clad	ASTM B506
Sheet, Lead Coated	ASTM B101
Sheet, Printed Circuits	ASTM B451
Strip	AMS 4500, ASTM B694, B152, SAE J463, J461
Strip, Building Construction	ASTM B370
Strip, Clad	ASTM B506
Strip, Printed Circuits	ASTM B451
Studs	ASTM F468
Tube, Bus	ASTM B188
Tube, Welded	ASTM B447
Wire, Coated With Lead Alloy	ASTM B189
Wire, Coated With Nickel	ASTM B355
Wire, Coated With Silver	ASTM B298
Wire, Coated With Tin	ASTM B246, B33
Wire, Flat	AMS 4500, ASTM B272
Wire, Hard Drawn	ASTM B1, FEDERAL QQ-W-343
Wire, Medium-Hard Drawn	ASTM B2, FEDERAL QQ-W-343
Wire, Metallizing	MILITARY MIL-W-6712
Wire, Soft	ASTM B3, B738, B48, FEDERAL QQ-W-343, SAE J461, J463
Wire, Stranded	ASTM B8, B496, B470, B286, B229, B226, B174, B173, B172, FEDERAL QQ-B-575
Wire, Trolley	ASTM B47, B116

Chemical Composition:

	Cu	O
Min/Max	99.90 min
Nominals	-	0.04

Fabrication:

Joining Technique	Suitability
Brazing	Good
Butt Weld	Good
Capacity for Being Cold Worked	Excellent
Capacity for Being Hot Formed	Excellent
Coated Metal Arc Welding	Not Recommended
Forgeability Rating	65
Gas Sheilded Arc Welding	Fair
Machinability rating	20
Oxyacetylene Welding	Not Recommended
Seam Weld	Not Recommended
Soldering	Excellent
Spot Weld	Not Recommended

Physical Properties:

Product Property	US Customary	Metric
Coefficient of Thermal Expansion	9.4 · 10 6? per °F (68-212 F)	16.9 · 10 6? per °C (20-100 C)
Coefficient of Thermal Expansion	9.6 · 10 6? per °F (68-392 F)	17.3 · 10 6? per °C (20-200 C)
Coefficient of Thermal Expansion	9.8 · 10 6? per °F (68-572 F)	17.6 · 10 6? per °C (20-300 C)
Density	0.322 lb/in3 @ 68 F	8.91 gm/cm3 @ 20 C
Electrical Conductivity	101%IACS @ 68 F	0.591 MegaSiemens/cm @ 20 C
Electrical Resistivity	10.3 ohms-cmil/ft @ 68 F	1.71 microhm-cm @ 20 C
Melting Point Liquid US	1981 F	1083 C
Melting Point Solid US	1949 F	1065 C
Modulas of Elasticity in Tension	17000 ksi	117000 MPa
Modulas of Rigidity	6400 ksi	44130 MPa
Specific Gravity	8.91	8.91
Specific Heat Capacity	0.092 Btu/lb/°F at 68 F	393.5 J/kg · °K at 293 K
Thermal Conductivity	226.0 Btu · ft/(hr · Ft2 · °F) at 68 F	391.1W/m · °K at 20 C

Sizes Available:

HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS	8mm To 100 mm
HEX	10mm To 60mm
SQUARE	10mm To 60mm
FLAT	10mm Min Thickness and max Width 120mm
BILLETS	Up to 200 mm
INGOTS	As per Specification