a182 316L stainless steel pipe fitting flanges ansi

 a182 316L stainless steel pipe fitting flanges ansi

• Type 316L has the same composition as Type 316 except the carbon content is held 

below 0.03%. Not unexpectedly, its general corrosion resistance and other properties 

closely correspond to those of Type 316. However, it does provide immunity to intergranular 

attack in the as welded condition or with short periods of exposure in the temperature range of 800 deg. - 1500 deg.F. The use of 316L is recommended when exposure in the carbide precipitation 

range is unavoidable and where annealing after welding is not practical. However, prolonged 

exposure in this range may embrittle the material and make it susceptible to intergranular attack.
• The maximum temperature for scaling resistance in continuous service is about 1650 deg. F. 

and 1500 deg.F. for intermittent service.
• May be susceptible to chloride stress corrosion cracking.
• Non-hardenable; non-magnetic in the annealed condition, and slightly magnetic when cold worked

Features:
1) Type: butt welded and seamless pipe fitting

2) Size: DN15-DN1200 (1/2"-48").

we can also produce other specifications according to customers' requirements .
3) Wall thickness: SCH5S-SCH160S.
4) Standard: ASME/ANSI B16.9, GB/T12459, GB/T13401, SH3408, SH3409, HG/T21635, HG/T21631, MSS SP-43, DIN 2605, JIS B2313.
5) Material: Stainless steel (304/304L, 316/316L, 317L,321, 321H, 310S, 347H , DUPLEX2205, S31803,904L,)
6) Applications range: For use in the petroleum, smelting, foodstuff, power, papermaking,
 chemical, medical equipment, aviation, boiler heat exchanger, and other fields.