Specifications
API 6A & AISI 75KCharpy impatc at -75degree Fahrenheit and the average value=55J
1.The forgings are made of the material ANSI4130(UNS G413300).
2.Minimum reduction ratio of product is 4:1.
3.Heat-treament :Q+T
4.The mechanical property is carried out at lab authorized National.
Yield=565Mpa,Tensile=711Mpa,Elongation=25%,Reduction=70% Headness(Avg)=221HB.
5.Impact at -60c(-75F):Longitudinal=50J Avg. Transverse=35J.(Specimen 10x10x55mm)
6.The visual & dimension & hardness on component are inspected & tested.
7.All procedures of making included heat-treatment are recirdered and machining are completed in our own forged shop,heat-treatment shop and machining shop.
4.All the procedures of production are recorded,so it is very easy to trace.
5.According to customer needs,we would have carry out the Intermational Third-Party Inspection(TPI) on products and have got EN10204 3.2 Certificate.
Send Inquiry to This Supplier
You May Also Like
-
DIN PN10/16 Ansi B16.5 Wn Flanges Carbon Steel SS304 Slip on Flange Plate Blind Flange for Industrial PipesUS$ 16.00 - 30.00MOQ: 20 Pieces -
Forged Round Bar of Electromagnetic Pure Iron for Electric Motor ComponentsNegotiableMOQ: 100 Kilograms
-
Pipe FlangeNegotiableMOQ: 2700 Pieces
-
Custom Hot Forging Parts Carbon Steel & Alloy Steel Forging Service for MachineryNegotiableMOQ: 1 Ton
-
Large Diameter Swing Bearing Gear With Custom Tooth Profile & Hardness HRC 58-62NegotiableMOQ: 1 Piece
-
Bolt Hole Plastic Valve and Flange Edge ProtectorNegotiableMOQ: 100 Pieces
-
For Electric Power Fitting Reusable Casting Parts With Machining SurfaceNegotiableMOQ: 100 Pieces
-
High-precision Carbon Steel Flange Customization Large Diameter Stainless Steel Flanging Butt Welding Flange Carbon Steel Flat Welding FlangeUS$ 1.5 - 100MOQ: 1 Piece
-
CNC Machining Parts Ductile Iron Material of Construction Engineering Fittings Parts FastenerUS$ 1 - 2MOQ: 1000 Kilograms
-
Forged Aluminum JointsUS$ 0.1 - 0.1MOQ: 100 Pieces