65% silicate zirconia milling ball for industrial ceramic use

65% silicate zirconia milling ball for industrial ceramic use

Description:
zirconium silicate beads are made from the high grade Australian zircon sand with granulating shaped method and hardened by sintering. The unique formula and producing procedure offer you a middle density and hardness, high wear resistance zircon beads. It is a good option to grind and disperse middle hard particles in low to middle viscosity range slurries. 

Items	unit	parameter
Composition	wt%	65% ZrO2 35% A2O3
Bulk Density	Kg/L	2.6~2.7(Φ2mm)
Specific Density	g/cm3	4.0~4.1
Hardness(HV)	GPa	>8.5
Elastic Modulus	GPa	200
Thermal Conductivity	W/m.K	3
Crushing Load	KN	≥8 (Φ7mm)
Fracture Toughness	MPam1-2	6.7
Grain Size	µm	≤0.8
Coefficient(20-400 °C)	10x10-6/ °C(20-400)	7.0

 

 

Sizes:

Application:

— Pigments and dyestuffs: to grind and disperse inorganic pigment such as TiO2, carbon black; organic pigments such as phthalocyanine blue, cromophtal yellow;

— Coatings & paints: protection paint, emulsion paint, printing inks, inkjet inks, paper coating and video tape coating;

— Fillers: Kaolin, Mica, CaCO3 and steatite.

Packing:25kgs/drum