ISO 1520 Cupping Tester Paint Cupping Test Machine Coating Flexibility Tester

1.Brief introduction

This testing machine has comprehensive functions and performance Meets the current national standards for cupping tests on metal sheets, aluminum and aluminum alloy sheets, and surface coatings of metal sheets,

2.The reference standards are as follows:

GB/T4156-2007  / ISO 20482"Erickson cupping test method for thin sheets and strips of metallic materials"

GB/T24524-2009 Test Method for Hole Expansion of Thin Plates and Strips of Metal Materials,

GB2611-92 General Technical Requirements for Testing Machines

JB/T7408-94 "Technical Conditions for Cup Bulge Testing Machine"

3. Main specifications

3.1. Sheet thickness: 0.01-3mm (high-precision sensor, capable of conducting ultra-thin sheet testing)

3.2. Board width: 90-100mm;

3.3. Punch stroke, 40mm;

3.4. Tighten the piston stroke by 40mm.

3.5. The maximum stamping load is 60kN.

3.6. The maximum clamping load is 10kN.

3.7. Cup protrusion resolution: 0.0025mm

3.8. Cup protrusion test mold specifications:

l  Standard punch ball: φ 20 ± 0.05mm

l  Standard pad mold aperture: φ 33 ± 0.1mm

l  Standard pad mold outer diameter: φ 55 (sample thickness 0.1-2) φ 70 (sample thickness 2-3)

l  Standard die aperture: 27 ± 0.05mm (sample thickness 0.1-2) 40 ± 0.05mm (sample thickness 2-3)

l  Standard die outer diameter: φ 55 (sample thickness 0.1-2) φ 70 (sample thickness 2-3)

3.9. Special orders can provide non-standard molds. Cup protrusion testing machine that meets international standards such as American and European standards.

3.10. Test speed: between 5mm/min and 20mm/min can be set freely and controlled accurately.

3.11. When a crack appears to penetrate the entire thickness of the specimen, the punch can immediately stop moving.

3.12. Hydraulic oil: N46 hydraulic oil.

3.13. Host dimensions: 800 × 760 × 1500 (mm)

3.14. Power supply AC380V, 50Hz.

3.15. Weight 510Kg.