Help CenterAlkali Resistance Firebricks Chromic Corundum Blocks Chrome High Alumina Refractory Bricks
Related Products
-
High Aluminum Fire Proof Blocks Firebricks Alumina Refractory BricksUS$ 300 - 550MOQ: 1 Ton -
High Performance Abrasion Resistant Sintered Phosphate Bonded High Alumina Refractory BricksUS$ 400 - 600MOQ: 1 Ton
-
High Alumina Fire Proof Blocks Insulating Firebricks Fireclay Refractory BricksUS$ 260 - 400MOQ: 1 Ton
-
Alkali Resistant Sintered Chrome Corundum Blocks Cr2O3 Alumina Firebricks Chromic Oxide Refractory BricksUS$ 1100 - 1400MOQ: 1 Ton
-
Low Silicon High Density Good Alkali Resistance Firebricks Chrome Corundum Brick Refractory BricksUS$ 900 - 1200MOQ: 1 Ton
Chrome Corundum Refractory Bricks
Introduction
Chrome Corundum Refractory Brick is kind excellent high temperature material, it contains 33~90% of Al2O3 and 1~30% of Cr2O3, mixed in a certain proportion, and made of special refractory production technology. It has the advantages of high refractoriness, high strength, good thermal shock stability, and strong corrosion resistance. good use effect.
Properties
The main ingredients of chrome corundum refractory brick are Al2O3 and Cr2O3, adding Cr2O3 to the Al2O3 single-phase refractory materials not only did not reduce the refractoriness of the materials, but the refractoriness increased with the increase of the Cr2O3 content.
Adding Cr2O3 to the corundum material, as the temperature rises, Al2O3 and Cr2O3 gradually form a solid solution, so that the corundum particles and the matrix are tightly combined, and further form a ring-shaped solid solution zone on the surface of the corundum particles, making the material tightly bond between particles and particles, particles and fine powder at high temperature, and the bonding phase is aluminum-chromium solid solution phase, which has a high melting point, and maintains bonding strength even at high temperatures. Therefore, chromium corundum refractory materials have strong mechanical properties at room temperature and high temperature.
Cr2O3 is a high-quality component in refractory materials, which can form high melting point compounds with a variety of oxides. For example, Cr2O3and Al2O3 can form a continuous solid solution. The melting point of this solid solution is above 2050℃. Cr2O3 and MgO/FeO form high-melting magnesia-chromium spinel/chromium iron spinel. Cr2O3 and Cu2O can form compounds with a melting point above 1600℃.
In addition, Cr2O3 can also increase the viscosity of the slag, and the increase of the viscosity of the slag can slow down the penetration rate of the slag into the refractory. In summary, Cr2O3 can improve slag erosion resistance and anti-spalling properties.
Chemical & Physical Index
Item |
XHJCC-15 |
XHJCC-10 |
XHJCC-5 |
|
Chemical Composition |
Cr2O3 % |
≥15 |
≥10 |
≥5 |
Al2O3 % |
≥75 |
≥80 |
≥85 |
|
ZrO2% |
≤1.0 |
≤1.0 |
≤1.0 |
|
Bulk Density g/cm3 |
≥3.35 |
≥3.3 |
≥3.2 |
|
Apparent porosity % |
≤18 |
≤18 |
≤18 |
|
Cold compressive strength MPa |
≥120 |
≥120 |
≥120 |
|
Load softening began to temperature °C (0.2Mpa,0.6%) |
≥1700 |
≥1700 |
≥1700 |
|
Characteristics
1.High refractoriness,usually the refractoriness is above 1700°C.
2.Refractoriness under load about 1500-1550°C because of poor high-temperature intensity.
3.Strong ability to resist basic (alkaline) slag,can not contact with acid refractory material.
4.Thermal shock resistance,so keep the temperature of furnace stabilized.
5.Poor Volume stability at high temperature,must set aside appropriate expansion joint when laying brick.
6.Strong ability of thermal conductivity,sometime need insulating material.
With the development of modern smelting technology, hot blast stoves generally adopt high air temperature technology, and the service life of hot blast stoves is required to be longer: therefore, higher requirements are put forward for the comprehensive performance of refractory materials for hot blast stoves. Damage to refractory materials used in hot blast stoves is usually caused by thermal stress, chemical attack, and mechanical loading. It is generally believed that an important reason for the damage of the hot blast stove is that the high temperature creep resistance of the refractory material is poor, resulting in collapse, deformation and cracking of the lining refractory material, thus causing widespread concern for low creep bricks for hot blast stoves.
Applications
Chrome Corundum Refractory Bricks are widely used in glass kiln lining, drawing glass flow hole cover tile and for the hot metal pretreatment device, waste incinerator, coal slurry pressurized gasifier lining and so on.
Packing
Wooden pallet, wrapped with plastic film & bundled belts
Send Inquiry to This Supplier
You May Also Like
-
Factory Price AZS Block Fused Alumina Zirconia Silica Corundum BricksUS$ 1500 - 2100MOQ: 1 Ton
-
High Heat Conductivity Silicate Bonded SiC Refractories Silicon Carbide Refractory BricksUS$ 600 - 999MOQ: 1 Ton
-
Professional Fireclay Brick Low Creep Refractory Thermal Insulation Fire Clay BricksUS$ 250 - 350MOQ: 1 Ton
-
High Wear Resistance General Fireclay Blocks Thermal Insulation Fire Clay Refractory BricksUS$ 210 - 350MOQ: 1 Ton
-
High Thermal Thock Stability Magnesite Aluminate Refractory Blocks Magnesia Alumina Spinel FirebricksUS$ 950 - 1050MOQ: 1 Ton
-
High Heat Spalling Resistance Magnesia Hercynite Firebricks Magnesia Iron Alumina Spinel BricksUS$ 950 - 1050MOQ: 1 Ton
-
High Thermal Conductivity Silicate Carbon SiC Refractories Silicon Carbide Refractory BricksUS$ 1000 - 1300MOQ: 1 Ton
-
Al2O3 Content High Alumina Fire Proof Bricks Insulating Firebricks Refractory BricksUS$ 300 - 1200MOQ: 1 Ton
-
Lightweight Mullite Bricks Thermal Insulation Fire Resistant K23 ~ K32 Insulating FirebricksUS$ 400 - 600MOQ: 1 Ton
-
Clay Refractory Brick Insulation Fire Clay Bricks SK23~SK34 Various Insulating Fireclay BricksUS$ 230 - 580MOQ: 1 Ton