Home > Products > Color Coated Aluminum Coil > RAL9003 color coated aluminum coil / PVDF aluminum coil inside diameter - 505mm
RAL9003 color coated aluminum coil / PVDF aluminum coil inside diameter - 505mm
- 0 Piece / Pieces per Month
- T/T L/C D/P D/A
- 7 days
- Brand new antminer Bitcoin miner T21 190T 3610W 19.0J/T BTC/BCH/BSV SHA256 Air-cooling Miner
- Yun Network Edge Network cable
- single mode sc connector SFP Module 1.25G 1310nm SFP 20km GLC-LH-SMD Cisco Huawei compatible
- INGKE, YKG-832429NL Direct Substitute XFGIGH-STKVDYD8-4,2X8 1000Base-T RJ45 Ethernet Connector Gigabit Magnetic Ethernet
- Cisco Power Injector (802.3at) for Aironet Access Points
- Aironet power injector AIR-PWRINJ5, 802.3af, 15.4W,Cisco Aironet- AP1140/1250/1260/3500/1600/1700/2600/2700/3600/3700 Series
Product Details
Brand Name: | ZhaoYang | Place of Origin: | China | Model Number: | color coated |
Product Description
Certification:ISO
RAL9003 color coated aluminum coil / PVDF aluminum coil inside diameter - 505mm
Polyvinylidene Fluoride Coatings (PVDF)
PVDF ( polyvinylidene fluoride ) is a chemical resistant thick film barrier coating commonly used in architectural applications where both excellent appearance and substrate protection must be maintained over a long period of time. This coating is unaffected by most chemicals and solvents and has excellent wear and abrasion resistance. PVDF also has a high dielectric strength, excellent resistance to weathering and the ability to self extinguish.
Polyester Coatings (PE)
PE ( polyester ) coatings exhibit an excellent combination of hardness, flexibility, flow, appearance, and superior resistance to dirt retention in indoor and outdoor applications. These coatings are highly resistant to abrasion, metal marking, staining, and marring, and require minimal maintenance. Glazetech uses polyester paints which provide excellent colour and gloss retention properties.
Category | Pre-coated abrasion-resistant aluminum sheet |
Acrylic pre-coated aluminum sheet |
|
Coating thickness | 25um | 20um | |
Pencil hardness | Breaking Scratching |
7H 5H |
2H |
Coin scratch resistance | 5 points method | 5 | 3 |
MEK resistance | Load 0.5kg | > 50 times | > 50 times |
Glossiness | Reflectivity 60° | 20 - 40% | 10 - 80% |
Coating adhesion | Matrix Erichsen test | 100 / 100 | 100 / 100 |
Impact resistance | DuPont's drop impact test 1/2"φ500g 50cm |
No swelling, no peeling | No swelling, no peeling |
Bending workability | OT bend test | ||
Salt spray resistance | Salt spray test 5%Nacl 35°C 1000 hours |
||
Humidity resistance | 40°C, RH95% 1000 hours | ||
Boiling water resistance | 8 hours | ||
Chemical resistance | 24-hour immersion in 5%H2SO4 at room temperature |
No color change | No color change |
24-hour immersion in 5%Hcl at room temperature |
|||
24-hour immersion in 5%NaOH at room temperature |
Chemical composition% | ||||||||||
Grade | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Al | |
1050 | 0. 250 | 0.400 | 0.050 | 0.050 | 0.050 | - | - | 0.050 | 99.50 | |
1060 | 0.250 | 0.350 | 0.050 | 0.030 | 0.030 | - | - | 0.050 | 99.60 | |
1070 | 0. 200 | 0.250 | 0.040 | 0.030 | 0.030 | - | - | 0.040 | 99.70 | |
1100 | Si+ Fe: 0. 95 | 0.05-0.2 | 0.050 | - | - | 0.100 | - | 99.00 | ||
1200 | Si+ Fe: 1. 00 | 0.050 | 0.050 | - | - | 0.100 | 0.050 | 99.00 | ||
1235 | Si+Fe: 0. 65 | 0.050 | 0.050 | 0.050 | - | 0.100 | 0.060 | 99.35 | ||
3003 | 0. 600 | 0.700 | 0.05-0.2 | 1.0-1.5 | - | - | - | 0.100 | remains | |
3004 | 0. 300 | 0.700 | 0.250 | 1.0-1.5 | 0.8-1.3 | - | - | 0.250 | remains | |
3005 | 0. 600 | 0.700 | 0.250 | 1.0-1.5 | 0.20-0.6 | 0.100 | - | 0.250 | remains | |
3105 | 0. 600 | 0.700 | 0.300 | 0.30-0.8 | 0.20-0.8 | 0.200 | - | 0.400 | remains | |
3A21 | 0. 600 | 0.700 | 0.200 | 1.0-1.6 | 0.050 | - | - |