Home > Products > Zinc Flake Coating > Water solution aluminium zinc coating , 20- 60s Spray Coating / 60-90S Dip - Spin Coating
Water solution aluminium zinc coating , 20- 60s Spray Coating / 60-90S Dip - Spin Coating
- 0 Piece / Pieces per Month
- T/T L/C D/P D/A
- 7 days
- Glass tube culture dish burette
- HC-M125 Multiple sizes test tube rack stainless steel/Portable Stainless steel test tube rack (18/30/40/60)
- HC-M125 Factory Price Stainless / aluminum steel test tube rack (18/30/40/60)
- Customize transparent inlet liner for Gas Chromatography NEPTUNE Plus Multiple Receiver Plasma Mass Spectrometer
- Round Bottom PTFE test tube 10ML OEM size pure white test tube
- 100ml Polytetrafluoroethylene PTFE test tube for lab
Product Details
Brand Name: | NFCase | Place of Origin: | China | Model Number: | AIA-1 |
Product Description
Certification:CE,FCC,MSDS
Technical Data Sheet
1 Product Information
Trade Name: Zincover
Article/Model No.:JH-9390
2 Composition/information on ingredients
JH-9390 is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and ethylene glycol. The radius-thickness ratio of Zn plate is 60~100.
Pack B: It is the solvent of the coating colored in orange-red and in water solution, which contain the Cr6+.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.
3 Coating Process
3.1 Mix Ratio
Pack A:16.0 kg
Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)
Pack C:0-50 g (according to different viscosity demand )
3.2
Mixture Method
Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.
3.2.2
Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃.
3.2.3
Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.
3.2.4
The coating should be filtrated by 80~100 mesh stainless steel screen before pouring into dip barrel.
3.2.5
Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.
3.2.6
Test density,PH,Temperature,Viscosity and Cr6+ content of coating every 8 hours if operate continuously.
5 Technical data
No. |
Item |
Data |
1 |
PH |
3.8-5.2 |
2 |
Cr6+ |
≥25g/L |
3 |
Specific gravity |
1.30±0.05 |
4 |
Viscosity |
20~60s(Spray Coating) ; 60~90S(Dip-Spin Coating) . 20℃ Zahn 2# cup |
5 |
Operating temperature |
20±2℃ |
6 Mix Diagram
Caution: Temperature should be controlled in above operation.
7 Coating Process
7.1 Degreasing
The workpiece should be degreased if there is oil on the surface. There are three processing methods:
1.High temperature
2.Neutral water-base degreasing agent
3.Organic solvent such as methylene chloride.
7.2 Derusting
The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.
7.3 Coating
The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.
7.4 Pre-heating
The workpiece after coated should be Pre-heated as soon as possible at 80~150℃ for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)
7.5 Curing
The workpiece after pre-heating should be cured at 300-340℃ for 20-40 mins. ( according to heat absorption of workpiece.)
8 Attentions
Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.
Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .
It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.
The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.
9 Packing
Pack A: |
16kg/ Metal Barrel |
Pack B: |
24KG Plastic Barrel |
Pa |
Contact Us
- Changzhou Junhe Technology Stock Co.,Ltd
- Contact nameMr. Lin
- Phone86-519-85922787
- Address20FL., Zhongchuang Budg., Times Commerce Plaza, 396 Tongjiamg Ave, Changzhou, Jiangsu, P. R. of Chin Changzhou,Jiangsu
- PTFE laboratory products 50ml PTFE test tubes virgin PTFE tube
- 1.5ml,5ml Freezing Vial Tube Screw Cap Cryo Tube
- Cotton plastic and wooden stick with medium swab
- High quality flat bottom glass test tube with aluminum screw cap
- 40 Holes Aluminum Test Tube Rack
- Metal Aluminum test tube rack test tube holder for laboratory/hospital
- Wholesale Plastic PET Vacuum PT Blood Tube with Sodium Citrate Addictive
- Test tube
- Urine sediment test tube
- 10ml PS Round Bottom Urine Test Tube with Cap
- Medical Testing Urinary Sediment Analysis Tube 12ml with Screw Cap
- Disposable PS PP Container 5ml Urine Sample Collection Test Tube without Cap
- Laboratory 10ml/25ml/50ml/100ml glass colorimeter tube
- High Borosilicate Glass 3.3 Colorimetic Tube
- Customized Glass Colorimetic Tube for Lab
- Transparent Glass 10ml/25ml/50ml/100ml Colorimetic Tube
- Glass Colorimetic Tube with glass hollow stopper
- Boro Glass Colorimetic Tube with glass hollow stopper
Popular Searches
Find Similar Products By Category
- Chemicals > Lab Supplies > Test Tube
- Buy on GoldSupplier.com
- How to Buy
- Browse by Catagories
- Browse by Hot Regoins
- Private Sourcing Events
- Sell on GoldSupplier.com
- How to Sell
- Post Products
- Manage Products
- Manage Groups
- About
- About Us
- Link to Us
- Contact Us
- Sitemap
- Please Enter your Email Address
- Please enter the content for your inquiry.
We will find the most reliable suppliers for you according to your description.
Send Now-
Mr. Lin
Welcome to my shop! Glad to serve you!Please send your question!
Your message has exceeded the limit.
Your message has exceeded the limit.
-
-
Your inquiry content must be between 20 to 5000 characters.Send Now.
-
Please input the mailbox.
-