Help CenterSecond Generation Zinc Aluminum Flake Corrosion Resistant Coating , Water Based Clear Coat
Related Products
-
Water Base Zinc - Al Flake Paint / Zinc Aluminum Flake CoatingUS$ 4 - 5MOQ: 1 Metric Ton -
JH-9088 Zinc Flake Coating , High Corrosion Resistance Aluminium Zinc CoatingUS$ 4 - 5MOQ: 1 Metric Ton
-
Junhetec JH-9201 Black Oxide Coating Agent for Carbon Steel , Alloy SteelUS$ 4 - 5MOQ: 1 Metric Ton
-
Junhetec JH-9382 Water - Base Micro Layer Corrosion Protection CoatingUS$ 4 - 5MOQ: 1 Metric Ton
-
Water Solution Aluminium Zinc Coating , 20- 60s Spray Coating / 60-90S Dip - Spin CoatingUS$ 4 - 5MOQ: 1 Piece
Certification:CE,FCC,MSDS
Technical Data Sheet
Zinc chromate coating is in today\'s world surface treatment alternative galvanized, hot galvanized, corrosion of high technology, surface treatment industry landmark significance of the times of products. We use the international advanced technology formula and foreign high quality raw material development and production of JH-9391, there is a major breakthrough in technology, is the preferred alternative to imported products.
1 Product Information
Trade Name: Zincover
Article/Model No.:JH-9391
2 Composition/information on ingredients
JH-9391 is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and ethylene glycol. The radius-thickness ratio of Zn plate is 60~100.
Pack B: It is the solvent of the coating colored in orange-red and in water solution, which contain the Cr6+.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.
3 Coating Process
3.1 Mix Ratio
Pack A:16.0 kg
Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)
Pack C:0-50 g (according to different viscosity demand )
3.2
Mixture Method
Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.
3.2.2
Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃.
3.2.3
Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.
3.2.4
The coating should be filtrated by 80~100 mesh stainless steel screen before pouring into dip barrel.
3.2.5
Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.
3.2.6
Test density,PH,Temperature,Viscosity and Cr6+ content of coating every 8 hours if operate continuously.
5 Technical data
|
No. |
Item |
Data |
|
1 |
PH |
3.8-5.2 |
|
2 |
Cr6+ |
≥25g/L |
|
3 |
Specific gravity |
1.30±0.05 |
|
4 |
Viscosity |
Adjust the viscosity according to the actual situation of the workpiece |
|
5 |
Operating temperature |
22±2℃ |
6 Mix Diagram
Caution: Temperature should be controlled in above operation.
7 Coating Process
7.1 Degreasing
The workpiece should be degreased if there is oil on the surface. There are three processing methods:
1.High temperature
2.Neutral water-base degreasing agent
3.Organic solvent such as methylene chloride.
7.2 Derusting
The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.
7.3 Coating
The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.
7.4 Pre-heating
The workpiece after coated should be Pre-heated as soon as possible at 80~150℃ for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)
7.5 Curing
The workpiece after pre-heating should be cured at 300-340℃ for 20-40 mins. ( according to heat absorption of workpiece.)
8 Attentions
Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.
Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .
It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and
Send Inquiry to This Supplier
You May Also Like
-
Mining Industry All Equipments and Products Exporting ServiceNegotiableMOQ: 1 Forty-Foot Container
-
1 Dollar Store Games Toy Product Cheap Swimming GogglesUS$ 0.05 - 0.3MOQ: 200 Pieces
-
Foshan Furniture Sourcing Collection Inspection Consolidation Storage Delivery ServiceUS$ 1 - 1,000MOQ: 1 Case
-
Warehouse Service to RussiaUS$ 1 - 9,999,999MOQ: 1 Cubic Meter
-
Trusted Yiwu Export Selling AgentUS$ 0.1 - 4MOQ: 1 Piece
-
2017 New Style Sterling Silver Opening Adorable Cat Ear Ring AgentUS$ 5 - 6MOQ: 20 Pieces
-
Sourcing and Buying Agent in Guangzhou ChinaUS$ 1 - 50MOQ: 1 Cubic Meter
-
B2B for Foreign Trade China Agent Foreign TradeUS$ 500 - 500MOQ: 1 Unit
-
Yiwu Trade Agent Buying Agent Bags Buying AgentUS$ 3 - 10MOQ: 1
-
Yiwu Market Mixed Container Service, Shipping Agent, Warehouing, Custom Clearance, Sourcing, Export, QC Service, TranslationUS$ 0.11 - 100MOQ: 10 Boxes