High Strength waterproof membrane for airport runway / sidewalks / road

High Strength waterproof membrane for airport runway / sidewalks / road

Product features

1. Good cohesive force: The sealant bonding strong with concrete, bricks, plastics, aluminum products, plastic products, galvanized plate and other material.
2. High strength and high elastic:Soft and high strength, Particularly suited to variant of the larger structure loop seal waterproof .
3. The weathering resistance, tear resistance, abrasion resistance, good penetration resistance.

Scope of application

1. Concrete buildings settlement joint and expansion joint, construction seam and metal structure of the seal waterproof.
2. For reservoirs, swimming pools, balcony, toilet bath rooms, through-wall pipe joint seal, etc.
3. The airport runway, sidewalks, roads, Bridges, square joint seal.
4. Prefabricated building roof panel, external wall panel, galvanized roofing sheet fracture repair, seal waterproof.
Construction process
A. joint treatment:
1. Before the construction must clean up the seams, using steel wire brush or shovel cleaning when necessary.
2. Deeper seam fill out plastic foam or hemp yarn as the backing material, the construction site must be dry.
B. Burdening: According to A component: B component = mass ratio of 1:2, pour A component into the B component ,and then use after mixture.

C. Construction operations:
1. When filling embedded horizontal seam, fill with good adhesive solution slowly in the joint gap until full.
2. Construction method of vertical fractures, when glue liquid condensed paste colloid as early, available extrusion ash knife or gun\'s embedded within the joint.

Packaging and specifications
1. Product packaging: Put A and B components according to the proportion in sealed packaging respectively, A and B components have obvious difference.
2. Packing specification: 30 kg/set

Reference dosage:1.3—1.4kg/㎡

Technical data
Density(g/cm3) 1.35±0.05
Touch Dry time(min) ≤180
Extrudability (ml/min) ≥80
Volatile content(%) ≤4
Sagging properties(mm) ≤1
Shore A-hardness(A) 30±5
Elongation at break(%) ≥600
Stretch modulus (23℃/Mpa) ≤0.4 (20LM)
Curing speed (mm/24h) 3~5
Elastic recovery rate(%) ≥80
Pollution properties Non
Application temperature(℃) +5～+35
Shelf life(month) 9