20MnV6, 42CrMo4, 40Cr Hard Chrome Plated Rod For Heavy Machine

20MnV6,  42CrMo4, 40Cr  Hard  Chrome  Plated Rod For  Heavy Machine

Hard chrome plated rod for heavy   machine

Detailed Product Description

1.Material:CK45,ST52,20MnV6,42CrMo4,40Cr

2.length:1000~8000mm

3.Diameter:6~1000mm

4.Ground and chrome plated

5.ISO9001:2008

Detailed Description

1.CHEMICAL COMPOSITION

Material	C%	Mn%	Si%	S%	P%	V%	Cr%
Ck45	0.42-0.50	0.50-0.80	0.04	0.035	0.035
ST52	0.22	1.6	0.55	0.035	0.04
20MnV6	0.16-0.22	1.30-1.70	0.10-0.50	0.035	0.035	0.10-0.20
42CrMo4	0.38-0.45	0.60-0.90	0.15-0.40	0.03	0.03		0.90-1.20
40Cr	0.37-0.45	0.50-0.80	0.17-0.37				0.80-1.10

2.MECHANCIAL PROPERTIES

Material	T.S  N/MM2	Y.S  N/MM2	E%(MIN)	CHARPY	CONDITION
CK45	610	355	15	>41J	NORMALIZE
CK45	800	630	20	>41J	Q + T
ST52	500	355	22		NORMALIZE
20MnV6	750	590	12	>40J	NORMALIZE
42CrMo4	980	850	14	>47J	Q + T
40Cr	1000	800	10		Q + T

3. SUPPLY CONDITION

    Ground  and  chrome plated 

4. CHROME THICKNESS

     20 to 30 micron

5. SURFACE ROUGHNESS

     Ra≤0.2 micron and  Rt≤2 micro

6. TOLERANCES ON DIA

    ISO f7 on the diameter

7.OVALITY

Half of the tolerance ISO f7

8. STRAIGHTNESS

   ≤0.2MM/M

9. SURFACE HARDNESS

   850-1150HV (vickers 100g)

10.COHESION

   No cracks,breaking or detaching after thermic shock(warming up at 300 celsius degrees and cooling

   in water)

11 .POROSITY

     Test according to ISO 1456/1458 and result yaluation according to ISO 4540 rating 8-10

12 CORROSION RESISTANCE

     Test in natural salt spray according to ASTM B 117-72hours

     Results evaluation according to ISO 4540 RATING 7-10

13. WELDABILITY

      Good

14. PACKING

     Anti rust oil to be applied on material and each rod to be packed in paper sleeve

15. CERTIFICATE

     All certificate relat