316 Hot Rolled Custom Cut Stainless Steel Sheet for Kichen Ware

Superior 304 Stainless Steel Sheet 

304 STAINLESS STEEL CHEMICAL COMPOSITION

C:≤0.08 

Si:≤1.00

Mn:≤2.00 
Cr:18.00-20.00
Ni:8.00-10.50
S:≤0.030  
P:≤0.045
MECHANICAL CAPACIYU:

Tensile Strength:σb (MPa):≥520

Yield Strength:σ0.2 (MPa):≥205

Elongation δ5 (%):≥40

Reduction of areaψ(%):≥60

Strength :≤200HV

Characteristics and application areas:

304 stainless steel with excellent stainless corrosion resistant performance and excellent intercrystalline corrosion resistance. With excellent cold and heat processing and forming performance. Be used in making cold heading,  deep drawing,  deep stretch forming parts.

With a good low temperature performance. In minus180 degreecelsius ,  strength ,  elongation ,  reduction of area are all good. Because there is no ductile brittle transition temperature,  usually used in low temperature . With good weldability ,  can use ordinary welding method ,  before and after welding don't need to heat treatment.

1.Materials(grade): 904L, 317L, 316TI, 316H, 316L, 316, 310S, 310H, 309S, 309H, 347, 347H, 321, 321H, 304H, 304L, 304, 301, 302, 303, 202, 304LN, 317LN, 310, 317, 314, 304TI, 321TI, 2520, 2205, 2304, 2507, 318, 303CU, 304CU, S31803, 317J1 and 316J1
2.standard:ASTM AISI GB DIN JIN
3. Thickness:0.3MM-80MM 

4. surface:No.1 / No.4 / BA / 2B / HL(bright annealed,  surface not oxidati and brighter) 

5. length:2000mm-6000mm or as customers requirement
6. width:1000mm-1500mm
7. packing:export stand picking ( swathe with waterproof paper , metal belt pack the sheet, then put them in the wooden pallet,  then put it in the container) or as customers requirement
8. Delivery time:within 10 days after we got your deposit
9. Payment:30% deposit 

10. Application:machine made industry, chemical industry, spin, shipping industry ,  architecture ,  food 

11. Delivery port:SHANGHAI, CHINA

12. Attention:we will supply you good quality and bottom price and firstclass service in china as hope to be your golden supplier. 

welcome to inquiry!