Fire Insulation Brick Lower Price High Alumina Brick

Specifications

High Alumina Refractories Brick
1.High temperature resistance
2.High strength
3.good heat-insulating

Fire Insulation Brick Lower Price High Alumina Brick

High alumina brick packing

 

 

High alumina brick refers to fire brick containing Al2O3 more than 48%, which is made of high 

grade bauxite through high temperature calcinations. High alumina brick is a kind of  neutral

refractory material so that it enjoys excellent resistance to acid and alkali corrosion. It has

characteristic of high refractoriness under load, which decide high alumina brick is an ideal 

material for various kinds of industrial furnace. It is widely used in building lining of hot-blast stove,

blast furnace, coke oven, rotary kilns of cement and so on.

 

 

High Alumina FireBricks
Dimension	230*114*65(mm)
Bulk Density	2.05,2.1-2.15, 2.3-2.4, 2.4, 2.5
Packaging Details	Pallet covering by PE membrane
Applications	Metallurgy, Chemical industry, Heat treatment furnace.

 

 

High alumina brick application

 

1.  Furnaces of metallurgy industry, heat treatment furnace

2.  Furnaces of chemical industry and construction industry

3.  Furnace of incineration of garbage, recirculating fluidized bad furnace

 

High alumina brick specification

Brand	SK-34	SK-36	HA-60	HA-70	HA-75
Al2O3(%)	>42	>50	>60	>70	>80
Fe2o3(%)	<2	<2	<2	<2	<2
Refractoriness	1750	1750	1770	1790	1790
refractoriness under load 0.2mpa(C)	1450	1450	1450	1510	1530
Porosity(%)	19-23	19-23	19-23	19-23	19-23
Bulk density(g/cm3)	>2.2	>2.3	>2.35	>2.4	>2.4
Cold cushing strength (mpa)	>30	>40	>45	>50	>60
Thermal expansion at 1000C(%)	<0.6	<0.6	<0.6	<0.6	<0.6

 

 

Characteristices of high alumina brick

 

1.High intensity for pressure

2. Good thermal shock stability

3. Strong abrasion and corrosion resistance 

4. High cold crushing strength 

5. Excellent abrasion resistance at cold and hot conditions

 

Advantages of high alumina brick

 

1 Excellent thermal stability
2 High refractoriness under load
3 Chemical stability and anti-corrision
4 Small high temperature creep rate
5 Excellent thermal shock resistance