High Flash Aluminium Paste

Technical  data sheet 

NonLeafing  aluminium paste –

solvent based (white spirit )

KCB1020

KCB1015

KCB1012

KCB1010

KCB1008

KCB1006

Structure 

Flake (lamellar )

ParticlesizeCILAS1064DD50

18

14

12

10

8

6

Soild (ISOR1247),min %

68

68

68

68

68

68

Solvent 

White spirit 

PROPERTIES

Brilliance 

<----------

Color saturation

<----------

Distinctness of image D01

---------->

Hiding powder 

---------->

Brightness  

<----------

APPLICATION

Industry

coating 

Industrycoating

coating 

coating

Coating 

Coating 

Industrycoating 

Industry  coating

Ink 

Ink 

Plastic 

Plastic

Ink 

Ink

Advices 

Pigmentation 

Binder and desired finish may have an impact on the rate of pigmentation.

Rate of pigmentation is about 3-20% (applied to finished varnish).

15-20% for anticorrosion coatings

3-4% for automobile finishes

Dispersing 

It is recommended pre-dispersion of the aluminum paste with solvent in ratio Al/S=

1:1 to 1:2 using stirrer with low shear forces or rapid dissolvers at maximum 4 m/s

peripheral speed

Cautions 

Deterioration of the optical effects could happen due to:

1.Heavy mechanical loads during production of coatings

2.Water containing solvents and additives

3.High acid values of components of coatings especially binders

4.Reactive components : chlorinated solvents, Pb based dryers

5.Low surface tensions will entail less brilliance of the paint.

Chlorinated solvents is not allowed in formulation. Avoid polar solvents.

Packing 

25kg/metal bucket    20container  fill 16.625MT  with pallet 

Storage and handing recommendation 

Store containers indoors keeping off the direct sunshine ,heat sources and water at temperatures

between 10 and 30C.

Keep ignition sources away.

Protect against electrostatic charges.

Avoid the contact with water, acid, alkali or halogenated compounds.

In the case of:

- Higher temperature it is possible the decrease of dispersability or the swelling of can by expansion of

the solvent

- At lower temperature: fatty acid is crystallized

Store containers tightly closed. Otherwise, is possible the drying of paste, contamination and the poor

dispersability due to evaporation of organic solvent and / or moisture absorption.

Separation means the situation where the organic solvent, bleeds onto the surface. It may be caused

when the impact or vibration is given to the container in excess. It is known to happen when the

container is transported after being long left in high temperature condition or in the case of being

subdivided. Such phenomenon does not mean the deterioration of aluminium paste. It can be used after

agitating well till it is mixed up uniformly.

Self life 

 12months 

Manufacture 

ji nan kingstyle metal pigments sciences&technology co.,ltd
http://kingstyle-metal.en.china.cn/
http://www.alpowder .com 

Skype :leyuan55

Cell phone :0086-18254114470

Person :miss Elva zhang