Help Center(SOLVENT-LESS)EPOXY RESIN SYSTEM PRIMER & TOP COAT EPOXY FLOORING MAYERIALS
Related Products
-
(TWO LIQUID TYPE)FLUOROCARBON RESIN LAQUER STEEL STRUCTURE PAINTUS$ 70 - 99MOQ: 1944 Sets -
(TWO LIQUID TYPE)RAL 3009 CORROSION RESISTANT FLUOROCARBON COATINGUS$ 70 - 99MOQ: 1944 Sets
-
(TWO LIQUID TYPE)RAL 5015 BLUE PAINT AND COATING FLUORINE PAINTUS$ 70 - 99MOQ: 1944 Sets
-
(TWO LIQUID TYPE) ANTICORROSION PAINT FLUOROCARBON SPRAY METAL TEXTURE PAINTUS$ 70 - 99MOQ: 360 Sets
-
MADE IN TAIWAN NIGHT NIGHT GLOW PAINT FLUORESCENT GLOW PAINTUS$ 50 - 62.5MOQ: 600 Units
(SOLVENT-LESS)EPOXY RESIN SYSTEM PRIMER & TOP COAT EPOXY FLOORING MAYERIALS
(SOLVENTLESS) EPOXY FLOOR COATING | |
TYPE |
A two-pack finish coating based on special solvent-less epoxy resin and hardener with chemicals resistance pigments. |
USES |
Anti-corrosive paint for chemical plants, power plants, steel factories. |
CHARACTERISTICS |
1. Tough and hard coat film with very good adhesion. 2. Brush one coat can obtain above 200 microns. 3. Excellent water and oil resistance 4. Excellent chemical resistance and anti corrosion. 5. Excellent mechanical wear resistance and electric insulation. |
COLOR |
Limited, please refer to color card |
GLOSS |
Above 85% |
DENSITY |
Above 1.35 Kg/L (mixture) |
VISCOSITY |
90 ~ 110 KU (25 ℃) |
DRYING TIME |
Set-to-touch 6 hrs. Dry hard 18 hrs. Full Dry 7 days (25 ℃). |
OPTIMUM FILM THICKNESS |
Wet 375 microns Dry 350 microns |
MIXING RATIO |
Base : Hardener = 15 : 4(by weight) |
POT LIFE |
30 minutes ( 25 ℃) |
NON-VOLATILE CONTENT |
Above 95% (mixture) |
THINNER |
Epoxy Thinner(cleaning tools only) |
THINNER RATE |
0 |
APPLICATION METHOD |
Trowel and brush. |
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
NOTE |
1. Mix base and hardener according to mixing ratio and stir thoroughly then use completely in five minutes. 2. Adhered moisture, grease, dirt, rusts and corrosive salts on substrate must be cleaned thoroughly. 3. Avoid applying the paint in rainy weather or humidity above 85% RH, particularly a wet surface must be thoroughly dried. 4. All equipments must be cleaned immediately after use. 5. When directly apply on the surface of cement products, the surface must be completely dried. 6. When overcoating interval is exceeded, the paint film must be roughened to insure adhesion. |
Send Inquiry to This Supplier
You May Also Like
-
Anti-static Self-leveling Epoxy Floor CoatingNegotiableMOQ: 1
-
PVC Coating Powder for Security Wire Mesh Fence - Enhanced DurabilityUS$ 2 - 5MOQ: 1000 Kilograms
-
Neon Colors Polyester Powder Paint Electrostatic Powder CoatingUS$ 1 - 9MOQ: 1 Kilogram
-
Titanium Dioxide Rutile Type 93% Used for Paint STD001 Shijiazhuang Standard ChemicalsUS$ 100 - 2000MOQ: 1 Ton
-
Aliphatic Polyurethane Paint for BuildingUS$ 1.8 - 8MOQ: 1000 Kilograms
-
Rotary Water Spray RoomNegotiableMOQ: 1 Set
-
EASY PAINTNegotiableMOQ: 2000 Pieces
-
Rubber Paint on SaleUS$ 1.45 - 35.21MOQ: 100 Pieces
-
Powder Coating EquipmentUS$ 75,000 - 950,000MOQ: 1 Set
-
Glass Car Body Coating From JapanUS$ 150,000 - 150,000MOQ: 1 Carton