Help CenterHDPE Waterproof Membrane
Related Products
-
Plastic Geogrid / Polypropylene Geogrid / Biaxial Geogrid / High Tensile Strength Geogrid /US$ 0.2 - 5MOQ: 1000 Square Meters -
High Quality GeotextileUS$ 0.5 - 1MOQ: 1000 Square Meters
-
1.5mm Thick UV-resistant Geomembrane High Strength Waterproof Membrane for Dam and Canal Lining BOLIUS$ 0.15 - 0.20MOQ: 10 Square Meters
-
High Adhesive, Water-proof, Anti Corrosion, Weather-resistant Asphalt Adhesive Glue Patch Cover for ConstructionNegotiableMOQ: 100 Rolls
-
Non-curable Rubber Paint Rubber Asphalt Waterproof Coating Made in ChinaUS$ 1.5 - 6MOQ: 500 Kilograms
Polymer Waterproof Membrane
By adopting modified masterbatch materials(EVA, PE, ECB), the polymer waterproof membrane is processed per standard GB/T 18173.1-2012. Its excellent flexibility and physical performance allow the product to be customizable, environmental-friendly and easier to assemble.
Applications
The waterproof &drainage of tunnels, expressways, railways, landfills and buildings.
The blockage of contamination in water channel, ditches and outlets.
The partition treatment of stony desertification, sandy desertification and salinization.
Product Properties for membrane(GB 18173.1-2012)
No. |
Property |
Product Standard |
Membrane |
|||
1 |
Sheet Thickness mm |
- |
1.2 |
1.5 |
2.0 |
|
2 |
Tensile Strength at Break MPa≥ |
16 |
17.2 |
17.5 |
17.2 |
|
3 |
Elongation at Break%≥ |
550 |
840 |
850 |
835 |
|
4 |
Tear Resistance(N/mm)≥ |
60 |
90 |
93 |
91 |
|
5 |
Impermeability(30min) |
0.3MPa without seepage |
0.3MPa without seepage |
|||
6 |
Cold Bend |
-35oC bend without crack |
-35oC bend without crack |
|||
7 |
Thermal Expansion and Shrinkage/mm |
Expansion |
2 |
2 |
2 |
2 |
Shrinkage |
6 |
6 |
6 |
6 |
||
8 |
Thermal aging(80oC×168 h) |
Retention rate of tensile break strength%≥ |
80 |
80 |
80 |
80 |
Retention rate of tensile break strength%≥ |
70 |
70 |
70 |
70 |
||
9 |
Alkali Resistance(normal temperature) Ca(OH)2 Saturated Solution×168 h |
Retention rate of tensile break strength%≥ |
80 |
80 |
80 |
80 |
Retention rate of tensile break strength%≥ |
90 |
90 |
90 |
90 |
||
10 |
Artificial Weathering |
Retention rate of tensile strength at break%≥ |
80 |
80 |
80 |
80 |
Retention rate of tensile strength at break% ≥ |
70 |
70 |
70 |
70 |
||
11 |
Peel Strength(between sheets) |
N/mm(standard test)≥ |
1.5 |
1.5 |
1.5 |
1.5 |
Retention Rate of Immersion(normal temperature×168 h)/%≥ |
70 |
70 |
70 |
70 |
||
Send Inquiry to This Supplier
You May Also Like
-
Low Cost Waterproof Material ManufactureUS$ 1,000 - 50,000MOQ: 1 Set
-
PTFE Architectural Membrane MaterialNegotiableMOQ: 1
-
Special Compound BaseUS$ 0.12 - 0.25MOQ: 7000 Square Meters
-
PolyLock/HDPE Lock/ E Lock/ HDPE E Lock/Geomembrane Attaches HDPE GeomembranesUS$ 10 - 50MOQ: 1 Piece
-
Breathable House Wrap Membrane Roofing Waterproofing MembraneUS$ 0.42 - 0.42MOQ: 5000 Square Meters
-
<MIicroVENT> Waterproof Vent MembraneUS$ 0.1 - 3MOQ: 10000 Pieces
-
Membrane Structure Entrance Gatehouses for Residential Communities, Membrane Structure School Stands, Production, Construction and Installation of Pvdf Membrane Structure Stadium RoofsUS$ 30.62MOQ: 900 Square Meters
-
Self Adhesive Polymer Modified Bitumen Waterproof MembraneNegotiableMOQ: 2000 Square Meters
-
Etfe Air Cushion Membrane Structure Roof, 1050 Pvdf Membrane Tube Truss Toll Stations, Gas Stations, and Charging Station Canopies, Ptfe for Sports Exhibition Venues, High-speed Railway Station Platforms, and Waiting HallsUS$ 61.38MOQ: 1000 Square Meters
-
Supply of Training Towers, Steel Structure Fire - Fighting Training Towers, Military Physical Training Iron Towers, Single - and Double - Window Climbing and Rope - Descending Training TowersUS$ 1000 - 1100MOQ: 5 Metric Tons