ESE 201/202/203 Self-adhesive Polymer Modified Bitumen Waterproof Membrane

ESE 201/202/203 Self-adhesive Polymer Modified Bitumen Waterproof Membrane

STAR factory ESE 201/202/203 Self-adhesive Polymer Modified Bitumen Waterproof Membrane adopts the technology of reinforcement while also use the high quality of asphalt materials to make the upgraded membrane higher extensible and more impact resistance, and also use the micron lap radian and activate the absorption process at the edge of the lap joint and the adhesive layer – this makes the activated molecules in the membranes generates a completed sealed non-trace lap with the lap joints, and to form a cross-linked reaction then a high strength adhesive power with the concrete base.

ESE 201 (Polyester Mat/Reinforcement)

Composed of base material, including synthetic rubber like SBS, good road asphalt and viscosity increaser.

Thickness Option: 2mm, 3mm, 4mm

Heat resistance: 60~70°C

Low temperature Flexibility: -30~-5°C

Peak Tension (N/50mm): 350~800

Elongation (Peak elongation/%): 30~40

Surface film: Polyethylene (double)/Aluminum/Sand, single side or both sides self-adhesive.

ESE 202 (Without Mat/Reinforcement)

Thickness Option: 1.2mm, 1.5mm, 2.0mm

Heat resistance: 70°C

Low temperature Flexibility: -30~-20°C

Peak Tension (N/50mm): 150~200

Elongation (Peak elongation/%): 30~200

Surface film: Polyethylene (double)/Aluminum/Sand, single side or both sides self-adhesive.

ESE 203 (With Aluminum foil)

Thickness: 1.2mm, 1.5mm, 2.0mm

Heat resistance: 70°C

Low temperature Flexibility: -30~-20°C

Peak Tension (N/50mm): 150~200

Elongation (Peak elongation/%): 30~200

Surface film: Polyethylene (double)/Aluminum/Sand, single side or both sides self-adhesive.