punching steel AISI1045/ DIN1.1191

Specifications

1.punching steel AISI 1045/ DIN1.1191
2.EAF& ESR material.
3.Hardness:HBS:<=229
4.Good wearable ability.

      punching steel AISI 1045/ DIN1.1191  

 

Introduction:

 

AISI 1045 Medium Carbon, Medium Tensile Steel, supplied black as rolled, black as forged or normalised and bright drawn or smooth turned, offering good strength, toughness and wear resistance. Will through harden in sections up to 63mm – with a tensile strength of 620 - 850 MPa.

 

 

Typical Chemical Analysis

Carbon	Silicon	Manganese	Phosphorus	Sulphur
0.45%	0.25%	0.75%	0.050% max	0.050% max

 

Related specifications:

AS 1442-1992	AS 1443-1994	BS970-3-1991	EN10083-1-1991	JIS G 4051	SAE &UNS	Werkstoff
1045 Black	1045 Bright	080A42 or 080A47	1.1191 C45E	S45C	1045&G10450	1.0503 C45

 

Typical Mechanical Properties – for guidance only

Finish	Yield strength MPa	Tensile Strength MPa	Elong %	Hardness HP
Cold Drawn	500-650	640-850	8 min	190-270
Smooth Turned	300-450	570-700	14-30	170-210
Hot Rolled/Forged	300-450	570-700	14-30	170-210

 

 

Typical Mechanical Properties – for guidance only

Water or oil quenched at 830°C – 850°C and tempered between 540°C – 680°C

Section mm	Yield Strength MPa	Tensile Strength MPa	Elong %	Lzod J	Hardness HB
Up to 63	370 min	620-850	11 min	30	185-245

 upplied to chemical analysis only unless ordered in the heat-treated condition

 

 

 

Welding procedure:

 

 

Low hydrogen electrodes are recommended. Pre-heat at 200°C –300°C and maintain during welding. Cool slowly in ashes or sand etc and stress relieve when this is possible. Welding details for guidance only.

 

 

HEAT Treatment:

 

 

Forging:

 

Heat to 1250°C Hold till uniform

 

Minimum forging temperature 850°C Cool in still air

 

 

Annealing:

 

Heat to 800°C – 850°C -- Cool in furnace

 

Normalising:

Heat to 870 °C - 920 °C -- cool in still air

 

Stress Relieving:

Heat to 550°C – 660°C---Cool in still air

 

 

Hardening:

 

Heat to 820°C – 860°C --- Quench in oil or water

 

Flame and Induction hardening:

 

Heat quickly t othe required case depth at  830°C – 860°C and quench immediately in water or oil. temperature at  will reduce stresses in the case with minimal effect on its hardness. all de-carburised surface material must firstr be removed to ensure best.

 

 

 

 

Delivery Condition

 

Forged + Annealed + Machining (Peeled/Turned)

 

 

 

Size Availability

 

We offer different types of steels, including square, flat and round.

 

 

 

 

 

 

 

Both electric steel and electroslag steel/Standard – Non-standard are available.  

 

 

Dimensional Tolerance:

The dimensional tolerance and the straightness of black “as forged” bar

can vary quite considerably. Bars should always be checked prior to machining to ensure that they will clean up as required.

 

Quality Assured Supply:

 

  

1045 carbon steel is supplied in accordance with our ISO 9001 : 2008 registration.

 

 

Typical Applications:

Axles, bolts, connecting rods, studs, rams, pins, rolls, spindles, ratchets, crankshafts, torsion bars, sockets, worms, light gears, guide rods etc.