Double coated tissue tape (substitute for 3M 55230)

Specifications

1good substitude for 3M55230
2good heat-resistant
3excellent double-stick
4strong sdhesion
5tape material:tissue

  TP5300-Double sidede adhesive tape(substitude for 3M55230)

1.       Product Description

TP5300 Double Coated Tissue Tape for dimensional stability and improved handling with ease of die cutting and laminating.The hign tack adhesive provides relatively high initial adhesion and good shear holding power to a variety of surfaces.

 

2.       Construction

TP5300
Face side 1 Adhesive Type/Thickness	Acrylate/0.003(0.076mm)
Backside 2 Adhesive Type/Thickness	Acrylate/0.003(0.076mm)
Liner Color,Type	White,120g PCK
Liner Caliper	0.0052(0.130mm)
Carrier Type	Tissue
Note 1:Faceside adhesive is on the interior of the roll,exposed when unwound.     2:Backside adhesive is on the exterior of the roll,exposed when liner is removed.

 

3. Typical Physical         Note : The following technical information and data should be considered            representative or typical only and should not be used for

Properties and         specification purposes.

Performance         

Characteristics

 

TP 5300
Adhesion to stainless steel ASTM D3330-180 degree,2 mil PET 30 minute RT	80(N/100mm)
Adhesion to AL ASTM D3330-180 degree,2 mil PET 30 minute RT	80(N/100mm)
Adhesion to other surfaces ASTM D3330-180 degree, 2 mil PET,30 minutes RT Shear strength-ASTM D3654	PCP   :65
	ABS   :80
(1 inch2 sample size)1000grams at 72(22)	5000 minutes
Relative solvent resistance	Medium-Low
UV Resistance	Medium
Relative High Temperature	Operating Ranges	Long Term(days,week) 70
		Short Term(minutes,hours)150
Shelf Life of Tape in Roll Form	24 months from date of manufacture when stored in original cartons at 70(21) and 50% relative humidity

 

4. Application      Bond strength is dependent upon the amount of adhesive-to-surface

Techniques      contact developed. Firm application pressure helps develop better adhesive contact and improves bond strength.

 

To obtain optimum adhesion, the bonding surfaces must be clean,

dry and well unified. Some typical surface cleaning solvents are isopropyl alcohol or heptane.

 

Note: Carefully read and follow the manufacturers precautions and directions for use when working with solvents.

 

Ideal tape application temperature range is 70°F to 100°F (21°C to38°C). Initial tape application to surfaces at temperatures below 50°F (10°C) is not recommended because the adhesive becomes too firm to adhere readily. However, once properly applied, low temperature holding is generally satisfactory.

 

5.General        All tapes have a film carrier, which can add dimensional stability to

Information      foams and other substrates. The carrier also provides easier handling during slitting and die-cutting.

 

 

6.Features        Adhesive is a medium-firm acrylic adhesive system featuring both high initial adhesion and good high temperature holding power.

 

 

7.Application      Medical/non-medical diagnostic test strips

Ideas             Plastic film lamination/bonding

Splicing

Foam lamination

 

 

8.Application      To apply adhesives in a wide web format, lamination equipment is

Equipment      required to ensure acceptable quality. To learn more about working with pressure-sensitive adhesives please refer to technical bulletin, Lamination Techniques for Converters of Laminating Adhesives.

 

9.Certification/      MSDS:  has prepared a MSDS for the products.

Recognition        TSCA: The product are defined as articles under the Toxic Substances Control Act and therefore,are exempt from inventory listing requirements.

ISO9001 ISO14001

                                      

 

 

 

 

This Engineered Adhesives Division product was manufactured under a  quality system registered to ISO 9001 standards and Environmental system registered to ISO 14001 standards