FR-Low smoke low halogen radiation cross-linked compound for wire & cable

Specifications

1. Flame-retardant
2. Suit to wire&cable
3. Permanent performances
4. Eco-friendly
5. Heat-stabilized

  

    Introduction

    Low-smoke low-halogen flame-retardant PE compound is based on PE, which is mixed with high grade flame retardant, smoke reduction agent and other process agent, to knead, plastify, and then extrude into pellets. It has excellent mechanical properties, flame-retardant property and processing properties. It can be used in power cable, control cable, optical cable and communication cable etc.

    MG80018 Low-smoke low-halogen flame-retardant polyolefin compound

    MG80018-105 105°C radiation cross-linked low-smoke low-halogen flame-retardant polyolefin compound

    MG80018-125 125°C radiation cross-linked low-smoke low-halogen compound

 

 

Test Items	Unit	Typical Value
		MG80018	MG80018-105	MG80018-125
Density(23°C)	g/cm3	1.4	1.41	1.39
Tensile strength	MPa	13.5	13.7	14.1
Elongation at break	%	220	210	230
Hot setting test	200°C x 15min, 0.2MPa
Elongation under load	%	-	90	75
Oven aging test	°C×h	100×136	136×168	158×168
Permanent elongation after cooling	%	-	5	6
Retention of Tensile strength	%	110	109	112
Retention of Elongation at break	%	86	88	87
low temperature brittleness	°C	-25	-25	-25
20°C Volume resistivity	Ω·cm	3.6x1013	2.6x1013	4.1x1013
Dielectric strength	MV/m	28	27	27
Oxygen index	%	31	32	31

 