Specifications
1. Enviromental friendly2. Flame-retardant
3. For extrusion
4. Weatherability
5. Excellent flexibility
Introduction:
Irradiation cross-linkable flame-retardant polyolefin low-Smoke non-halogen compound is based on polyolefin resin, which is mixed with non-halogen flame retardant, cross-linkable agent, and other process agent, to knead, plastify, and then extrude into pellets. It has excellent mechanical property, oil resistance, electirc property, flame-retardant property and processing properties. Moreover, it features the advantage of no halogen and low smoke amount giving out, which can be used in power cable, control cable, marine cable, optical cable and signal cable etc.
MG80017-90(J/H) 90°C irradiation cross-likable Flame-retardant polyolefin low-Smoke non-halogen insulating(sheating) compound
MG80017-105(J/H) 105°Cirradiation cross-linkable Flame-retardant polyolefin low-Smoke non-halogen insulating(sheating) compound
MG80017-125(J/H) 125°C irradiation cross-linkable Flame-retardant polyolefin low-Smoke non-halogen insulating(sheating) compound
| Test Items | Unit | Typical Value | ||
| MG80017-90(J/H) | MG80017-105(J/H) | MG80017-125(J/H) | ||
| Density(23°C) | g/cm3 | 1.45 | 1.44 | 1.45 |
| Tensile strength | MPa | 12.3 | 12.7 | 13.1 |
| Elongation at break | % | 220 | 210 | 200 |
| Hot setting test | 200°C x 15min,0.2MPa | |||
| Elongation under lood | % | 65 | 70 | 80 |
| Permanent elongation after cooling | °Cxh | 121x168 | 136x168 | 158x168 |
| Retaintion of Tensile strength | % | 109 | 112 | 110 |
| Retaintion of Elongation at break | % | 89 | 87 | 85 |
| low temperature impact Brittleness | °C | -25 pass | -25 pass | -25 pass |
| 20°C Volume resistivity | Ω.cm | 5.6x1014 | 3.7x1014 | 4.5x1014 |
| Dielectirc strength | MV/m | 26 | 28 | 27 |
| Oxygen index | % | 34 | 35 | 33 |
| Acid gas emission | mg/g | 0 | 0 | 0 |
| pH | 5.9 | 6.0 | 5.8 | |
| Conductivity | μs/mm | 0.8 | 0.7 | 0.5 |
| Dm(1.0mm) Smoke density | flame | 56 | 61 | 54 |
| non-flame | 152 | 159 | 162 | |
Irradiation dosage:
Irradiation dosage is different from the cable and da, genlerally 10-15MRAD recommended.
♦ Variety Colours
♦ Workshop show
♦ Company Certifications:
◊ ISO 9001:2008
◊ ISO 14001:2004
◊ Certification of UL
Send Inquiry to This Supplier
You May Also Like
-
HIPS Taiwan Chimei PH-888G Injection Molding Grade With High Impact StrengthUS$ 1 - 1.02MOQ: 1 Kilogram
-
Formosa FORMOCON POM FM090 for Precision Mechanical Gears, Bearings, and Automotive ComponentsNegotiableMOQ: 1 Kilogram
-
Polypropylene PP Resin K8009 - High Rigidity Homopolymer for Automotive PartsNegotiableMOQ: 1 Kilogram
-
Polymers & ResinsNegotiableMOQ: 2000 Bags
-
Celanese 70G30HSLR Zytel Nylon PA66 70g30hslr Bk099/101f Nc010/ 70g33L/103hsl/ 101 Nc010 Plastic PA66 Nylon 66 GranulesUS$ 3.1 - 3.4MOQ: 25 Kilograms
-
Eco-Friendly Thermosetting Powder Coating - Epoxy Polyester & Fluorocarbon Options for Metal SurfacesNegotiableMOQ: 500 Kilograms
-
Economic Interlocking Horse and Cow Stable Mat Made of Rubber or EVAUS$ 13.5 - 35.4MOQ: 100 Pieces
-
SAP Super Absorbent Polymer for Sanitary Napkins or DiapersUS$ 1.5 - 2MOQ: 1000 Kilograms
-
Slip Additive Masterbatch With PE CarrierUS$ 2.3 - 2.5MOQ: 500 Kilograms
-
UHMW PE Powder for Lead-acid Battery SeparatorUS$ 2,750 - 2,850MOQ: 1 Ton