plastic mould steel tool steel plate(s136/din1.2083/4cr13)

YAOTENG Steel are stockholders and suppliers of s136 stainless tool steel round bar, flat bar, plate and block. Rectangular pieces can be sawn from flat bar or block to your specific sizes. Diameters in 1.2083 can be sawn to your required lengths as one offs or multiple cut pieces. Ground tool steel bar can be supplied, providing a quality precision finish to tight tolerances.

s136 stainless tool steel is ideally suited for plastic moulds, for acid aggressive plastics,

PVC or acetates, and can be used with plastics containing abrasive fillers. It also is suitable to produce components for medical and optical applications.

Forge by heating slowly and uniformly to 1000°C. After forging cool slowly in furnace or thermoinsulating material.

Heat slowly to 780°C. Cool slowly in furnace at a slow rate to 600°C and then cool in air.

When heavy machining and/or grinding has been carried out, stress relieving is advisable to minimise the danger of distortion or cracking during the subsequent heat treatment. To stress relieve, heat the tools slowly to 650°C, soak for a minimum of two hours per 25mm of section and allow to cool down in the furnace to 500°C then continue to cool freely in air. The tools can then be finish machined, leaving on an allowance for final grinding after hardening and tempering. 

Pre heat the  600-700°C until heated through. Continue heating the to the final hardening temperature of 980-1050°C and allow the component to be heated through. Protect the component against decarburisation by using a neutral salt bath, controlled atmosphere furnace or vacuum. Air cool or quench in oil.

Heat the 1.2083 uniformly and thoroughly to the selected tempering temperature and hold at heat for one hour per 25mm of total thickness. Double tempering is recommended. To achieve the best permutation of hardness, toughness and corrosion resistance it is recommended to temper at 250°C.

Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each s136 steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult your heat treatment provider for full guidance on heat treatment of stainless tool steel.

1.2083 S136 stainless tool steel is supplied in accordance with our ISO 9001 : 2008 registration.

Hot work tool steel

DIN

1.2344,1.2343,1.2365,1.2581,1.2367,1.2713 etc.

AISI

H13,H11,H10,H21, etc.

JIS

SKD61,SKD6,SKD5,SKT4 etc.

Cold work tool steel

DIN

1.2601,1.2379,1.2080,1.2363,1.2842,1.2419,1.2510,1.2550,1.2767 etc.

AISI

D2,D3,D5,D6,D8,A2,O2,O1 etc.

JIS

SKD1,SKD11, SKS3 etc.

Plastic mould steel

DIN

1.2083,1.2311, 1.2316,1.2738 etc.

AISI

P20, P20+Ni, 420 etc.

JIS

NAK80

High speed tool steel

DIN

1.3355,1.3343

AISI

T1,M2,M35,M42

JIS

SKH2,SKH51

Structural alloy steel

DIN

1.7225,1.6511,1.7035,1.7220

AISI

4,140,434,051,404,130

JIS

SCM440

Tel:        +86-0769-3389 9333

Fax:       +86-0769-8870 5839

Skype:    lara.liao80

Email:      laraliao AT toolsteel DOT net DOT cn

               lara AT otaisteel DOT com

TM:        cn1511348531

Mobile:   86 13711884714