Best Price Hot Sale Tantalum Target/disk/tantalum Sputtering Target

Chemistry                                                                %

Designation

Chief component

Impurities  maxmium

Ta

Nb

Fe

Si

Ni

W

Mo

Ti

Nb

O

C

H

N

Ta1

Remainder

0.004

0.003

0.002

0.004

0.004

0.002

0.03

0.015

0.004

0.0015

0.002

Ta2

Remainder

0.01

0.01

0.005

0.02

0.02

0.005

0.08

0.02

0.01

0.0015

0.01

Diameter, inch (mm)

Tolerance, +/-inch (mm) 

 0.125~0.187 excl (3.175~4.750)

0.003 (0.076) 

 0.187~0.375 excl (4.750~9.525)

0.004 (0.102) 

 0.375~0.500 excl (9.525~12.70)

0.005 (0.127) 

 0.500~0.625 excl (12.70~15.88)

0.007 (0.178) 

 0.625~0.750 excl (15.88~19.05)

0.008 (0.203) 

 0.750~1.000 excl (19.05~25.40)

0.010 (0.254) 

 1.000~1.500 excl (25.40~38.10)

0.015 (0.381) 

 1.500~2.000 excl (38.10~50.80)

0.020 (0.508) 

 2.000~2.500 excl (50.80~63.50)

0.030 (0.762) 

    Rod, Diameter 0.125" (3.18mm)~2.5" (63.5mm)

 Grade

Tensile strength, psi (MPa), ≥ 

Yield strength, psi (MPa), ≥ 

Elongation in 1 inch gage length, %, ≥ 

 RO5200/RO5400

 25000 (172)

 15000 (103) 

25 

 RO5252

 40000 (276)

 28000 (193) 

 20

 RO5255

 70000 (482)

 55000 (379)

 20

 RO5240

 40000 (276)

28000(193)

Physical Properties

Tantalum

Atomic Number

180.95

Density

16.6 g/cc

Melting Point

3290 K, 2996°C, 5462°F

Boiling Point

5731 K, 6100°C, 9856°F

Coefficient of Thermal Expansion (20°C)

6.5 x 10(-6) / °C

Electrical Resistivity (20°C)

13.5 microhms-cm

Electrical Conductivity

13% IACS

Specific Heat

.036 cal/g/°C

Thermal Conductivity

.13 cal/cm(2)/cm°C/sec

Annealed

Ultimate Tensile Strength

285 M Pa (41 ksi)

Yield Strength

170 M Pa (25 ksi)

% Elongation

30%+

%Reduction in Area

80% +

Cold Worked

Ultimate Tensile

650 M Pa

Strength

(95 ksi)

% Elongation

5%

Hardness

Annealed

90 HV

Cold Worked

210 HV

Poisson's Ratio

0.35

Strain Hardening Exponent

0.24

Elastic Modulus Tension

186 G Pa (27 x 10(-6) psi)

Ductile Brittle Transition Temperature

< 75 ° K

Recrystallization Temperature

900 - 1200 °C