Cemented Carbide Strips for Wood Cutting Tool

Grade

Enquivalent

To ISO

Density

(g/cm3)

HRA

T.R.S

(Mpa)

Application

YG6

K10

14.8

≥90.0

≥2150

High wear resistance, used for hard wood, used for processing original wood, 

aluminum section bar, brass rod and cast iron.

YG6A

K10

14.9

≥92.0

≥1860

Higher wear resistance than YG6, used for processing hard wood, original wood, 

aluminum section bar, brass rod and cast iron.

YG8

K20-30

14.8

≥89.5

≥2320

High wear and percusstion resistance,used for processing hard wood, soft wood, 

ferrous and non ferrous section bars.

YS2T

M10

14.8

≥92.0

≥2350

Fine grain alloy, high wear resistance, high anti-bending strength, high resistance

 to bonding, high thermal strength. 

Machining of refractory alloys, stainless steel and high manganese steel, etc.

YS25

P25

13.8

≥91.0

≥2200

High hardness and good wear resistance, suitable for rough turning, 

milling and planing of carbide steel, cast steel, high intensity steel and steel alloy.

YL10.2

14.5

≥92.2

≥2150

Wear resistance and strength comparatively higher, suitable for processing cast iron, 

non-ferrous and non-metal materials.