Tungsten Carbide Inserts for Milling Steel Material

Grade

Enquivalent

To ISO

Density

(g/cm3)

HRA

T.R.S

(Mpa)

Application

YG6

K10

14.8

≥89.5

≥2150

Suitable for the semi-finishing and finishing of non-ferrous metals and nonmetallic materials, for finishing milling and finishing milling of continuous sections and for broaching,etc.  

YG6X

K10

14.8

≥91.7

≥1860

Suitable for machining chilled alloy, cast iron and heat resistant alloy with good performance. It is also suitable for the finishing of normal cast iron. 

YG8

K20-30

14.8

≥89.7

≥2060

Suitable for the intermittent rough turning, planing and milling of uneven surfaces of non-ferrous metals and nonmetallic materials. And it is also used for drilling of normal holes and depth holes and for broaching.

YT5

P30

13.2

≥89.5

≥1560

Suitable for the heavy duty rough turning of steel and cast steel with a big feed rate at a medium and low speed under unfavorable working conditions.

YT14

P20

13.0

≥90.5

≥1400

Suitable for the finishing and semifinishing of steel and cast steel.

YT15

P10

13.1

≥91.0

≥1300

S Suitable for the finishing and semifinishing of steel and cast steel with a moderate feed rate and a rather high cutting speed.

YS8

M05

13.9

≥92.5

≥1720

It can be used for the finishing of iron based and nickel based high-temerature alloys and high strength steel and it can be also used for the finishing of chilled cast iron, heat resistant stainless steel,high manganese steel and hardened steel.

YC30S

P30

13.8

≥90.0

≥1600

Used for the milling of steel and cast iron, with high performance of crack-resistance and toughness.