CHEAP WATER-BASED ANTI FIRE INTUMESCENT FIRE RESISTANT SPRAY PAINT

PRODUCT NUMBER

FW-30

TYPE

The water-based fire retardant coating based on nonflammable resin with special pigment and additives, which will be inflated with the fire or heat to form a fine foam layer. This foam layer can insulate substrates to contact with the fire, therefore consumedly cut down flammability of flammable substrates and retard the transmission of heat and the expansion of fire.

USES

Used for interior wood furniture, RC wall of buildings and interior decoration.

CHARACTERISTICS

1. Very fast drying for recoating in a short time.

2. Use the water thinner without any pollution.

3. Inflated above several times when occurred the fire to rapidly reach the fireproof and fire-retardant effects.

4.Carbonized foam body can resist high temperature up to 1000℃

COLOR

White or desired colors

SPECIFIC GRAVITY

1.35 ± 0.05 Kg/L

FINISH

Flat

VISCOSITY

90± 10 KU (25 ℃)

DRYING TIME

Set-to-touch 0.5 hr.  Dry hard 2 hrs (25 ℃)

OVERCOATING INTERVALS

Min.   2 hrs.

NUMBERS OF COATING

1.CNS 6532 class 3 :   min. 3 times

2. ASTM E84 class A :   min. 2 times

OPTIMUM FILM THICKNESS

1.  CNS 6532 class 3 :   Wet   205   microns   /   Dry   110   micron

2.  ASTM E84 class A :   Wet   150   microns   /   Dry   80   microns

THEORETICAL COVERAGE

1.CNS 6532 class 3 :   734 g/meter square     (6.9 meter square  /Gal)

2. ASTM E84 classA :                                

150 ft2/Gal(13.9 meter square   /Gal)

THINNER

Water

THINNING RATE  

Max.   25%

VOLUME SOLIDS  

Above   60%

STORAGE SHELF LIFE  

Minimum 6 months under normal storage conditions.  

APPLICATION METHOD  

Spray,Brush.

FIREPROOF TEST  

Meet CNS 6532 class 3 and ASTM E84 class A(ULFile No. R13583)

NOTE

1.Before application, stir paint evenly, when paint is too thick, water can beadded within specified quantity.

2.  Adhered moisture, grease, rust, dirt or loose paints film on substrate must be cleaned thoroughly.

3. Rough the smooth surface with sand papers and avoid applying the paint in humid exceed 85% RH or temperature low to 5℃

4. The fireproof effect and dry film thickness of fire retardant coating is in direct proportion, namely the dry film thickness is more thick and the intumescent effect of paint film is better, the fireproof effect is better too.