Ingredients:
Unsaturated polyesters resins, modified resin, color pigment, stuffing, anti sediment materials, auxiliary agent and firming agent mixing ratio 100：2.
Characteristics:
Good scratching performance, outstanding adhesive force and elasticity. Resistance to temperature change and some certain of baking. Mainly being applied to the leveling up and decoration of the blemishes, such as the drop pits of keelsons, pin-shaped cavities, crackles, and little welding lines etc. before closing the floating coat in the painting technics of furniture, building material and auto. Satisfying the leveling and smoothness of the keelsons before painting the surface. It is also of good repairing performance for glass reinforced plastics.
Main technical standard:
|
Item |
Index |
Testing Standard |
|
Outward appearance |
The color is unanimous, and there are no visible particles by naked eye. |
Visual examination |
|
Air drying |
Meet the customers’ requirements |
GB/T1728-79 |
|
Consistency |
9-12cm (except for the specialities) |
GB/T1749 |
|
Scratching performance |
Good handling, no curling (suitable for broad scratching) |
|
|
Burnishing performance |
Burnishing performance is very good |
|
|
Resistance to high temperature |
There is no bubbling and cracking under baking at 170℃ after drying |
|
|
There is no bubbling and cracking under baking at 100℃ after gelling |
|
|
|
Pliability |
≤80mm |
GB/T1748 |
|
Resistance to temperature change |
More than 2 cycles |
|
|
Impact Strength |
≥13kg.cm (or 35kg.cm Not falling off) |
GB/T1732 |
|
Adhesive force |
≥60Kg/1.2cm2 |
GB/T5210 |
Reference for construction:
1、 Evenly mix the main ash and firming agent with the proportion being 100：2 (make the color unanimous), and using up them within the gelation time.
2、 Scratch the putty which has already finely mixed on the primer paint of double components after burnishing or the surface of cold-rolled sheet which has already been finished processing. If the thickly scratching is required, you’d better thinly scratch for many times to meet the required thickness. If some air bubbles infiltrate while scratching, you should thoroughly strickle it by means of scraper, so as to ensure the good adhesive force. The best wet milling time is 0.5-1h after scratching.2-3h is the best dry milling time.
Notes:
1、 Once the putty mix firming agent, don’t put it into can and cover it after using in case that the impregnant volatilization may result in the deterioration of main ash.
2、 The solidifying period of coating film will extend if the temperature is high or low. The consistence and gelation time of putty may adjust according to the requirements of customers’.
3、 This product is unsuitable for directly scratching on galvanization plates.
4、 Its quality can be guaranteed for 6 months since the date of its production. If it does not beyond this period, it can be used continuously.
Send Inquiry to This Supplier
You May Also Like
-
Sodium Gluconate Cas 527-07-1 25kgUS$ 100 - 2000MOQ: 1 Ton -
PET Woven Filter Cloth for Filter PressUS$ 1 - 15MOQ: 1 Piece
-
Chemical AuxiliariesNegotiableMOQ: 2400 Kilograms
-
Non-Stick PTFE Release Spray for Die Casting - FDA Compliant FormulaUS$ 1 - 4MOQ: 200 Kilograms
-
Zeolite Carbon Sieves 3a 4a 13x Adsorbent for Oxygen Concentrator Generator Molecular SieveNegotiableMOQ: 1
-
Modified Starch for Paper IndustrialUS$ 630 - 650MOQ: 5 Tons
-
NA Cmc Powder Food GradeUS$ 550 - 3,690MOQ: 5 Tons
-
Diapers Baler Hydraulic Pressing Baling MachineUS$ 3,200 - 3,250MOQ: 1 Set
-
Leather Wall Panel for Background and Ceiling PanelUS$ 3 - 6MOQ: 200 Pieces
-
AC Blowing Foam Blowing Agents of AzodicarbonamideUS$ 2,100 - 2,680MOQ: 1 Ton