ALL CATEGORIES

Home > Packaging & Printing > Package & Conveyance > Foam Packaging > PET Cellophane For Printing Or Laminating

PET Cellophane For Printing Or Laminating

US$ 1.19 - 1.49 MOQ: 3000 Kilograms

Key Specifications

Material:

PET

Type:

Stretch Film

Usage:

Packaging Film

Hubei Yifeng Import & Export Co., Ltd.

Payment & Shipping

Payment Methods:

Port of Shipment:

Shanghai Port

Delivery Detail:

Delivery time depends on order quantity.

Material PET

Type Stretch Film

Usage Packaging Film

Feature Moisture Proof

Hardness Soft

Processing Type Multiple Extrusion

Transparency Transparent

Place of Origin Zhejiang, China

Brand Name Yif

Model Number Polyester-T

More details, please contact with maggie(mobile/whatsapp: 0086-15586203120)

Product Description

BOPET Packaging Film is a three layer co-extruded, biaxially oriented film.

PET transparent film is widely used for aluminizing, printing, complexing.

Main Features

Excellent strength and dimensional stability;

Good flatness;

Excellent chemical satbility;

Good surface properties.

Properties		Test Methods	Units	Typical Values
Thickness		GB/T 6672	micron	12	25	36	50	75
Tensile Strength @100mm/min	MD	ASTM D882	N/mm²	190	190	190	190	190
Tensile Strength @100mm/min	TD	ASTM D882	N/mm²	200	200	200	200	200
Elongation at Break	MD	ASTM D882	%	110	120	130	130	140
Elongation at Break	TD	ASTM D882	%	100	110	120	120	130
Modulus of Elasticity	MD	ASTM D882	N/mm²	4000	4000	4000	4000	4000
Modulus of Elasticity	TD	ASTM D882	N/mm²	4300	4300	4400	4400	4400
Coefficient of Friction	Static	ASTM D1894	--	0.55	0.55	0.55	0.55	0.55
Coefficient of Friction	Dynamic	ASTM D1894	--	0.50	0.50	0.50	0.50	0.50
Surface Wetting Tension	Treated	GB/T 14216	mN/m	56	56	56	56	56
Surface Wetting Tension	Untreated	GB/T 14216	mN/m	42	42	42	42	42
Heat Shrinkage	MD	302°F(150°C) 30min	%	1.8	1.7	1.5	1.5	1.1
Heat Shrinkage	TD	302°F(150°C) 30min	%	0	0	0	0	0
Gloss @45°		ASTM D2457	%	129	129	129	129	129
Haze		ASTM D1003	%	3.0	3.0	3.0	3.0	3.0
Total Luminous Transmission		ASTM D1003	%	90.0	90.0	90.0	90.0	90.0