FRP Exterior Wall Panel

Specifications

1.good Performance of film
2.flat and smooth. Dust is easy to be removed
3.good corrosion resistance
4.good impact strength

                                       Welcome to Locwid Company

 

1. Product information

 

FRP gel coat flat sheet is solidified and composited by gel coat, polymer resin and glass fiber.  It is a new eco-friendly product developed by our company .It can be widely used in making high grade panels of vehicles, refrigerated vans,purification,medical treatment and food engineering etc.  It can instead of colored steel plate, stainless steel plate, aluminum plate and PVC plate etc. With good features of high strength, hardness, smooth surface, wear-resistance, corrosion resistance, aging resistance, cleanliness and bacteria resistance. etc. The thickness can be adjusted easily(1.0mm~5.0mm), and packaged in rolls and sizing.

 

2. Performance

 

<1> Smooth surface, light weight, anti-aging, anti-corrosion

<2> suitable for acid and alkali environment.

<3>Always used on truck body, container, inside board of the refrigerator, ceiling panels, commercial, civil construction and public facilities interior walls and ceiling. Modified car, or other special purpose transport outer panels etc.

 

3. Technical parameter

 

No	Item	Technical data	Value	Result	Test method
1	Oxygen index (%)	≥27	27.2	pass	GB/T 2406-1993
2	Horizontal Burning , (class)	FH-1	FH-1	pass	GB/T 2408-1996
3	Vertical Burning ,(class)	FV-1	FV-1	pass	GB/T 2408-1996
4	Tensile strength (MPa)	/		pass	GB/T 1447-2005
5	Flexural strength(MPa)	/	263		GB/T 1447-2005
6	Low temperature impaction	-40°C×1h	10/0 pass		GB/T 8814-2004
7	transmittance %	/	86.8		GB/T 2410-1980
8	Water absorption %	/	0.38		GB/T 17657-1999
9	Barcol hardness	/	51		GB/T 3854-2005
10	Distortion temperature(1.81Mpa)	/	Above 260		GB/T 1634-2004
11	Heat conductivity 25°C W/(m•k)	/	0.648		GB/T 10297-1998
12	Modulus of elasticity in static bending	Gpa	6.1		GB/T 1447-2005
13	Acid resistance	/	No change in surface		Refer to GB/T 4218-1984
14	Alkali resistance	/	No change in surface		Refer to GB/T 4218-1984
15	Loading performance,mm	≤30	6	pass	JC/T 562-1994

 

4. Application