HDPE resin for making bags

Physical Properties

Nominal Value

Density       g/cm3

0.921

Melt Mass-Flow Rate (MFR) g/10min

1.9

Shore Hardness (shore D)

45

Tensile Modulus  MPa

175

Tensile Strength MPa

Yield, 

9.0

Break,

13.0

Tensile Strain(Break) %

850

Modulus of Elasticity MPa

250

Vicat Softening Temperature°C

89.0

Melting Temperature (DSC) °C

108

Peak Crystallization Temperature (DSC) °C

97.0

Heat of Fusion J/g

110

Volume Resistivity ohm •cm

8.5E+15

Dielectric Strength kV/mm

30.0

Dielectric Constant (60Hz) %

2.20

Dissipation Factor (60 Hz)

0.00050