CaO 1.0 ~ 1.5% fire resistant brick-magnesite-chrome brick

Specifications

magnesite-chrome brick
1.Magnesite chrome brick of alkaline slag erosion resistance is strong,
2. good thermal shock resistant

Magnesite-chrome brick

 

 

Product usages

 

 

Used for building steel furnace, furnace refining furnace, non-ferrous metal smelting furnace, cement kiln, glass kiln, etc.

 

 

Production process

 

 

Production technology of calcined magnesite chrome brick and magnesite chrome bricks in line. In order to eliminate

 the bricks in burning process because of MgO style and Cr2O3, Al2O3, or directly combined magnesite chrome 

brick. The main raw material of manufacturing magnesite chrome brick is sintered magnesite and chromite. Magnesia raw material purity as high as possible, chromite 

chemical composition requirement is: the Cr2O3:30 ~ 45%, CaO: 1.0 ~ 1.5% or less.

 

 

Classification

 

 

Brick according to the physical and chemical indicators divided into MGe - 20, MGe - 16, MGe - 12, MGe - 8 four grades

Refractory temperature: 1580 ~ 1770 °C (°C)

 

 

Technical index

 

 

Kind	direct-bonded magnesia-chrome bricks								semi-rebonded magnesite-chrome brick
	MGe8A	MGe8B	MGe12A	MGe12B	MGe16A	MGe16B	MGe18A	MGe18B	MGe16A	MGe16B	MGe20A	MGe20B
MgO  % ≥	74	74	66	66	60	60	58	58	60	60	55	55
Cr2O3% ≥	8	8	12	12	16	16	18	18	16	16	20	20
SiO2 % ≤	1.5	2.0	1.5	2.0	1.5	2.0	1.5	2.0	1.5	1.8	1.5	1.8
apparent porosity% ≤	18	18	18	18	18	18	18	18	17	17	17	17
cold crushing strengthMPa ≥	40	35	40	35	40	35	40	35	40	35	40	35
Load softening point°C  ≥	1660	1600	1660	1600	1660	1600	1660	1600	1750	1700	1750	1700

 

 Photo