Contact Platform Support
Help CenterHigh Luster,elegance,rigidity 304 Stainless Steel Sheet Price
Related Products
-
Reasonable Price 304 Stainless Steel Sheet /plate is AvailableUS$ 1,000 - 3,000MOQ: 1 Metric Ton -
Black Matte Finish 201 304 316 316L Stainless Steel Sheets in China 1.4304/FactoryUS$ 1,000 - 3,000MOQ: 1 Metric Ton
-
S.S 304 Good Cold Rolled Stainless Steel Sheet Rich StockUS$ 1,000 - 3,000MOQ: 1 Metric Ton
-
ISO9001 Standard S.S 304 Stainless Steel Sheet Manufacturer From ChinaUS$ 1,000 - 3,000MOQ: 1 Metric Ton
-
Rich Stock 201 304 430 BA Stainless Steel Sheet for SaleUS$ 1,000 - 3,000MOQ: 1 Metric Ton
316Ti Stainless Steel Hot Rolled Sheet
316Ti Summary
316 Ti, the titanium-stabilised version, is used for its resistance to sensitization during prolonged exposure in the 550oC-800oC temperature range.
316Ti Chemical Composition (ASTM A 240)
|
C |
Mn |
P |
S |
Si |
Cr |
Ni |
Mo |
Ti |
SX316 |
0.08 max |
2.0 |
0.045 |
0.030 |
1.0 |
16.0 |
10.0 |
2.00 |
- |
316Ti Mechanical properties at room temperature
|
SX316 |
SX316L |
SX316Ti |
|||
|
Typical |
Minimum |
Typical |
Minimum |
Typical |
Minimum |
Tensile Strength, MPa |
580 |
515 |
570 |
485 |
600 |
515 |
Proof Stress (0.2 % offset), MPa |
310 |
205 |
300 |
170 |
320 |
205 |
Elongation (Percent in L = 5.65 So) |
55 |
40 |
60 |
40 |
50 |
40 |
Hardness (Brinell) |
165 |
- |
165 |
- |
165 |
- |
Erichsen Cup Test Value mm |
8 - 10 |
- |
10 - 11 |
- |
- |
- |
Endurance (fatigue) limit, MPa |
260 |
- |
260 |
- |
260 |
- |
316Ti Properties at elevated temperatures
The values given refer to SX 316 and SX 316 Ti only as strength values for SX 316L fall rapidly above 425oC.
Short Time Elevated Temperature Tensile Strength
Temperature, C |
600 |
700 |
800 |
900 |
1000 |
Strength, MPa |
460 |
320 |
190 |
120 |
70 |
316Ti Corrosion Resistance
The performance of SX 316 compared with other metals in various environments is shown in the
following table. Corrosion rate is based on a 5 year exposure.
Environment |
Corrosion Rate (mm/year) |
||
SX 316 |
Aluminium-3S |
Mild Steel |
|
Rural |
0.0025 |
0.025 |
5.8 |
Marine |
0.0076 |
0.432 |
34.0 |
Marine-Industrial |
0.0051 |
0.686 |
46.2 |
Note: For corrosion resistance of SX 316 relative to other types, see the section in Comparative Data.
316Ti Annealing.
Heat from 1 010oC to 1 120oC and cool rapidly in air or water. The best corrosion
resistance is obtained when the final annealing temperature is above 1 070oC.
316Ti Stress relieving.
Heat from 200 - 400oC and air cool.
316Ti Hot working
Initial forging and pressing: 1150 - 1200oC
Finishing temperature: above 900oC
For upsetting operations, forgings
should be finished between: 930 and 980oC
All hot working operations should be followed by annealing.
Our Products:
Packing:
Our Advantage:
1) Big manufacture original materials (TISCO BAOSTEEL ZPSS LISCO)
2) Five years stainless steel exprience
3) Professional suggestions
4) Customers around the world
Send Inquiry to This Supplier
You May Also Like
-
Stainless Steel Plate for Chemical Processing - 317L/904L Corrosion ResistantNegotiableMOQ: 1 Ton
-
Professional Manufacturer Bar Set Stainless Steel Aisi 310h Stainless Steel Bar Stainless Steel Bar/RodNegotiableMOQ: 1 Ton
-
Premium Customized Cold Rolled Stainless Steel Coil 300 SeriesUS$ 1000 - 4000MOQ: 1 Ton
-
Brass Woven Wire Sieves 316L Steel Grade Plain Weave 20-200 Mesh 15cm/35cm Diameter Industrial Grading SievesUS$ 4.7 - 15MOQ: 1 Piece
-
ASTM Aluminium Pure Sheet Corrosion Resistance 6065 Aluminium PlateNegotiableMOQ: 1 Ton
-
Stainless Steel Double Ferrule Compression Fittings With 5000 PSI RatingNegotiableMOQ: 500 Pieces
-
Punched and Stamped 316 430 201 304 Stainless Steel PlateUS$ 0.1 - 0.1MOQ: 100 Pieces
-
201 Stainless Steel PlateUS$ 800 - 10,000MOQ: 5 Tons
-
304 2B ss Sheet /304 BA ss SheetUS$ 600 - 1,000MOQ: 3 Metric Tons
-
Hand Tools,ISO9001,UAKS,the Equipment of Releasing the Static (stainless Steel),non Magnetic ToolsUS$ 44.5 - 98.6MOQ: 10 Pieces