welding wire used for welding 500 MPa low alloy steel

Specifications

welding wire used for welding 500 MPa low alloy steel
1.stable arc
2.low splashing
3.high deposited efficiency
4.CE/CCC/ISO

welding wire used for welding 500 MPa low alloy steel  

 

characteristics:

1. stable arc

2. low splashing

3. high deposited efficiency

4.CE/IS9001/CCC   

 welding wire used for welding 500 MPa low alloy steel    

    Non-copper coated welding wire GB ER50-6 is similar with AWS ER70s-6 is the first mass-produced non-copper coated welding wire manufacturer in china(mainland). It is used for welding 500 MPa low alloy steel single and muti-pass welding; also for high speed thin plates,pipe line steel welding.Suitable for manual welding, automatic welding and robot welding,such as oil machinery, heavy crane machinery, pressure vessels,oil-chemical vessels, ship body, bridge, constrction steel structure,ect.

 

2.Main Characteristics:

 

1,              No copper and less harm to the operator,environmental protection;

2,              ARC stability and reliable

3,              Good ARC

4,              Less spatter,and less smoke

5,              Feeding stability

6,              High strength and forming better

7,              Antirust and conductivity

8,              Less abrasion to the conductive nozzle.

 

 

3.Max Chemical composition(%):

 

 

Physical Characteristics:

 

AWS	Min Tensile strength	Min Yield srengrh	Min Elongtion	Akv (J)Room temperature
ER50-6	540Mpa	420Mpa	29%	90

 Uses:The welding consumable in use process is higher than common welding voltage 1 to 2 volts, current constant.

 