concrete polycarboxylate superplasticizer HPEG 2400

Concrete Polycarboxylate Superplasticizer Monomer HPEG/TPEG-2400

Water Reducing/Slump Retention type

DD-424    Modified HPEG2400

Advantages

1. This product is produced by high active catalyst and special process, which makes it in light color appearance.
2. This product has good selectivity, high double bond retention rate, which can dramatically increase the yield of the water reducing agent products, thus reduce the production cost of the water reducing agents.

Characteristics:
1. The water reducer from this material(HPEG2400) has good adaptability to cements.
2. Compared with other polycarboxylate materials, the production cost of water reducer from this material is greatly reduced.

3. The water reducing rate of the water reducer (solid content 22%) from this material is amount to 30% under 1.1% concrete addition.
4. The water reducer from this material is characterized by early strength,  high-strength, the early strength and 28 days’ strength of the concrete is greatly improved, compressive strength ratio %: 1 Day ≥180: 7 Days≥170; 28 Days≥ 150.
5. The water reducer from this material has high durability,can efficiently reduce the water/gel ratio, enhance durability, reduce shrinkage and creep.
6. The water reducer from this material has less slump loss, which grows initially, and won’t influence the strength, it also has sustained release effect, slump retention is ≥190 mm.
7. The water reducer from this material is environment friendly, chloride ion is not more than 0.1%, comply with the ISO 14000 international environment protection management standard.

Technical Specification

Chemical Structure: 

CH2=CCH3O(CH2CH2O)nH

Storage and Transportation
It is non-toxic, non-flammable and can be shipped as general chemicals, stored at dry, ventilated place, away from sunshine and rain.
Packing:  25 kg plastic bags with PE  liners                                         Validity: One year

Note: Above description is just for reference guidance, final performance will be determined by the test under local experimental enviroment.