POLYOLS FOR HIGH ELASTOMER FLEXIBLE FOAM

BRAND

HYDROXY VALUE

mgKOH/g

ACID VALUE

mgKOH/g

WARTER CONTENT

%

pH

UNSATURATED

VALUE

mol/kg

VISCOSITY

mPa·s/25°C

K+ %

COLOURITY APHA

EP-330N

32-36

≤0.05

≤0.05

5-7

≤0.07

800-1000

≤0.0003

≤50

EP-3600

26-30

≤0.06

≤0.05

5-7

≤0.08

1000-1600

≤0.0005

≤50

EP-3033

31.5-34.5

≤0.1

≤0.1

5-7

-

-

≤0.001

≤100

BRAND

HYDROXY VALUE

mgKOH/g

WARTER CONTENT

%

pH

PARTICLE SIZE

(ppm)

VISCOSITY

mPa·s/25°C

POP31/28

26-29

≤0.05

7-10

-

≤5000

POP36/28

25-29

≤0.05

6-9

-

≤3500

POP42-I

29-33

≤0.10

5-8

-

≤6000

POP42-II

29-33

≤0.10

5-8

-

≤6000

HPOP40

20-23

≤0.05

6-9

-

≤8000

POP48

27-30

≤0.10

6-9

-

≤9000

ZR-001

24-29

≤0.10

6.5-10.0

≤100

2000-3000

BRAND

MAIN APPLICANTIONS

EP-330N

HIGH REACTIVITY POLYETHER MIXED WITH BRANCHES AND POP TOGETHER .USED IN PRODUCING HIGH RESILIENCE, COLD CURED FOAM FOR AUTOMOBILE, MOTORCYCLE, BICYCLESEATS,STEERING WHEELS.

EP-3600

HIGH REACTIVITY POLYETHER MIXED WITH POP TOGETHER USED IN PRODUCING HIGH RESILIENCE, COLD CURED FOAM FOR AUTOMOBILE, MOTORCYCLE, BICYCLE SEATING, STEERING WHEELS AND POLYURETHANE ELASTOMERS.

EP-3033

MIXED WITH BRANCHES AND POP TOGETHER. USED IN PRODUCING  HIGH RESILIENCE COLD CURED FOAM FOR AUTOMOBILE, MOTORCYCLE, BICYCLE SEATS AND STEERING WHEELS.

POP31/28

USED IN AUTOMOBILE OF HIGH ELASTICITY SEATS,ARM RESTS AND STEERING WHEELS.

POP36/28

USED IN MOULD FOAM, SUCH AS CUSHIONS OF AUTOMOBILE, FURNITURE, MATTRESS.ETC.IT CAN STRENGTHEN THE LOAD-BEARING CAPACITY OF THE FOAM PRODUCTS.

POP42-I

USED IN CUSHIONS OF AUTOMOBILE, FURNITURE, MATTRESS AND HIGH-BEARING FLEXIBLE

FOAM.   

POP42-II

USED IN CUSHIONS OF AUTOMOBILE, FURNITURE, MATTESS AND HIGH-BEARING FLEXIBLE

FOAM.   

HPOP40

USED IN MOULD FOAM, SUCH AS CUSHIONS OF AUTOMOBILE, FURNITURE, MATTESS.ETC.IT CAN STRENGTHEN THE LOAD-BEARING CAPACITY OF THE FOAM PRODUCTS.

POP48

USED IN AUTOMOBILE INTERIOR TRIM,FURNITURE, MATTRESSES. ETC .AND ULTRA HIGH-HARDNESS FLEXIBLE FOAM, THERMAL-MOULD FOAM.

ZR-001

USED IN FLAME RETARDANT FOR HIGH ELASTOMER FOAM ,COLD-MOULD FOAM,SEMI-RIGID FOAM, INTEGRAL SKIN FOAM AND INJECTED MOULD.