Help CenterAnodized Aluminum l Profile Handle for Kitchen Cabinet
Related Products
-
G Shaped Handle Aluminum Alloy Profile for Kitchen Cabinet by China ManufactoryUS$ 2.5 - 10.5MOQ: 300 Pieces -
L Shape Handle Aluminum Extrusion ProfileUS$ 2.5 - 10.5MOQ: 300 Pieces
-
G Shape Anodized Matt Aluminium Profile Handles for Kitchen CabinetUS$ 2.5 - 3.5MOQ: 300 Kilograms
-
White New Alloy 6063 Series Anodized Edge Aluminium Profile For CabinetUS$ 2.5 - 3.5MOQ: 300 Kilograms
-
High Quality L Shaped Handle Aluminum Frame Profile for Kitchen Cabinets by China ManufacotoryUS$ 2.5 - 10.5MOQ: 300 Pieces
Anodized aluminum l profile handle for kitchen cabinet
This below model is 008.002.029
This below model is 036.037
The below model is 054,066,115
The below model is 109,273
Factory Information:
| Factory Establishment: | Established in 2008 year |
| Sister Factory: | XINHE ALUMINUM |
| Annual Production Capacity: | Over 100000 tons |
| Product Quality Grade: | high-precision level of GB5237 standard |
| Certification: | ISO9001 |
Product Information:
| Colors: | silver, champagne, gold, bronze, white, black, olive, green, blue, red, grey, iron grey, etc. |
| Surface treatment: | mill finish, sandblasting, anodizing, powder coating (spraying), electrophoresis, anodized polishing, mechanical polishing, brushing, plastic insulation, spraying wood grain, electrophoresis wood grain, PVDF coating, etc. |
| Length: | Any length as per customer's request, anodized maximum length is 6.7m |
| Thickness: | 0.8mm (+/-0.1mm) or customized |
| Maximum Extrusion Size: | 300mm x 185mm |
| Price: | 2500USD-3500USD/TON |
| Packaging: | protective film, pearl cotton / fleece, shrink film, poly bag, kraft paper, or as per customer's request |
| Payment Term: | 30% deposit payment + 70% balance payment |
| Delivery Time: | 20 to 30 days after receiving 30% deposit payment |
Production Equipment:
| Machine Name | Quantity | Country of Origin |
| environmentally friendly renewable fuel reflection casting furnaces and hot top type horizontal casting production equipment with high thermal efficiency | 8 | England |
| extrusion production lines | 46 | Taiwan and Japan |
| powder coating production lines | 3 | Switzerland |
| anodized color electrophoretic coating production lines | 4 | Japan |
| advanced sandblasting machines | 8 | China |
| advanced brushing machines and mechanical polishing machines | a dozen | China |
| large scale advanced anodized polishing production lines | 2 | China |
| crystal-phoresis production line | 1 | China |
| fluorocarbon coating production line | 1 | China |
| metal heat transfer printing wood grain production lines | 10 | Italy |
| thermal insulation plastic inserting machines | 2 | China |
| thermal insulation plastic infusion machine | 1 | China |
If you can not find the item you want,Please send us the profiles drawing of you need,
we can opening mould as requirement of customers
If you have any question,do not hestitate to contact us.
Factory Website: /en/index.php
Contact persons:Edward
Skype:tian.longbiao
cell phone:+86 18702624106
Factory Introduction:
Guangdong Yaoyinshan Aluminum Industry Co., Ltd rising in 2008 is a modern production and technology power, specializing in professional development and production of building, decorative and industrial aluminum alloy materials. The company is located in Baishi Industrial Development Zone, Genghe Town, Gaoming District, Foshan City, Guangdong Province, covers an area of 300,000 square meters, with an annual production capacity of over 100,000 ton, it has more than 1800 employees, including 298 senior and intermediate engineers and technicians and management staff. Factory Picture:
Factory Information:
General Chemical Composition of Alloy:
| ALLOY | 6061 (%) | 6063 (%) | 6063A (%) |
Si |
0.40 - 0.80 | 0.20 - 0.60 | 0.30 - 0.60 |
| Fe | 0.70 | 0.35 | 0.15 - 0.35 |
| Cu | 0.15 - 0.40 | 0.10 | 0.10 |
| Mn | 0.15 | 0.10 | 0.15 |
| Mg | 0.80 - 1.20 | 0.45 - 0.90 | 0.60 - 0.90 |
| Cr | 0.04 - 0.35 | 0.10 | 0.05 |
| Zn | 0.25 | 0.10 | 0.15 |
| Ti | 0.15 | 0.10 | 0.10 |
| Others (each) | 0.05 | 0.05 | 0.05 |
| Others (total) | 0.15 | 0.15 | 0.15 |
| Al | Remainder | Remainder | Remainder |
Mechanical Properties of Sections under Room Temperature:
(Not less than) (≥) Tensile strength test Hardness test
| Alloy | State | Tensile strength Mpa | Non-proportional stretching stress | Stretching rate % | Sample thickness mm | HV | HW |
| 6061 | T4 |
180 |
110 | 16 | - - | - - | - - |
| 6061 | T6 | 265 | 245 | 8 | - - | - - | - - |
| 6063 | T5 | 160 | 110 | 8 | 0.8 | 58 | 8 |
| 6063 | T6 | 205 | 180 | 8 | - - | - | - |
| 6063A | T5 | 200 | 160 | 5 | 0.8 | 65 | 10 |
| 6063A | T5 | 190 | 150 | 5 | 0.8 | 65 | 10 |
| 6063A | T6 | 230 | 190 | 5 | - - | - - | - - |
| 6063A | T6 | 220 | 180 | 4 | - - | - - | - - |
Anodic Oxidation of Aluminium Profile Finishing:
| Class of thickness | Minimum average film thickness / μm | Minimum local film thickness / μm |
| AA10 | ≥ 10 | ≥ 8 |
| AA15 | ≥ 15 | ≥ 12 |
| AA20 | ≥ 20 | ≥ 16 |
| AA25 | - - | ≥ 25 |
Note: Generally, our anodized aluminium profiles are produced as per grade AA10, or according to client's special request.
Electrophoresis of Aluminium Profile Finishing:
| Class of thickness | Anodic oxidation film thickness on measuring part / μm | Lacquer film thickness on measuring part / μm | Combined film thickness on measuring part / μm |
| A | ≥ 9 | ≥ 12 | ≥ 21 |
| B | ≥ 9 | ≥ 7 | ≥ 16 |
Note: Generally, our electrophoresis aluminium profiles are produced as per grade B, or according to client's special request.
The comparison table of Powder Coating (Spraying) of quality level between European Qualicoat standard and Xinyin standard:
| Item | Test | Qualicoat Standard | Xinyin Standard |
| Gloss | ISO2813 GB/T9754 | L-G: +5, M-G: +7, H-G: +10 | L-G: +5, M- G: +7, H-G: +10 |
| Thickness of coating | ISO2360 GB/T4957 | Average of five points is not less than 60μm. | Average of five points is not less than 60μm. |
| Adhesion | ISO2409 GB/T9286 | up to grade 0 | up to grade 0 |
| Erichsen cupping test | ISO1520 GB/T9573 | 5 mm | 6 mm, no crack |
| Impact test | ASTMD2794 GB/T1732 | 2.5 NM | 5.5 NM, no crack |
| Hardness test | ISO2815 GB/T6739 | at least up to 80 | not less than H |
| Resistance to cracking on bending | ISO1519 GB/T6742 | 5 mm | 5.5 mm, no crack |
| Mortar resistance test | ASTMC-207 GB/T1594 | The mortar must be easy to be removed without leaving any residues. | No removal, no visible change |
| Acid test | AAMA 2603 | Corrosion from lineation within 0.5mm | No air bubble, goffer or removal, etc.! |
| Salt spray resistance test | ISO9227 GB/T10125 | 1000 hrs | 1000 hrs; Corrosion from lineation within 2mm. |
| Resistance to boiling water test | AAMA 2603 | 1 hrs | 1 hrs; No any defect, such as air bubble, goffer, water spot or removal, etc.! |
| Artificial accelerated aging test | DIN553231 Suntest GB/T1865-97 | 1000 hrs; The loss of gloss must be not more than 50%. | Good! |
| Moisture resistance test | DIN50017 GB1740 | 1000 hrs | Good! |
| Solvent resistance | AAMA 2603 |
- - | No any defect, such as air bubble, goffer, water spot or removal, etc.! |
| Color difference test | - - | - - | E*ab ≤ 1.5 |
Send Inquiry to This Supplier
You May Also Like
-
Plastic End Caps for Aluminum Profile Railings Pipe and TubeUS$ 0.07 - 0.36MOQ: 120 Pieces
-
Customized China Manufacturer Aluminum Heat SinkNegotiableMOQ: 1
-
All Sizes Slotted Aluminum Channel/Upright at Wholesale PriceNegotiableMOQ: 1000 Pieces
-
LED Heat Sink Precision Made of Aluminum OEM ServiceUS$ 3.5 - 5.5MOQ: 1000 Pieces
-
Custom Anodizing Aluminum Heat Sink for Led LightsUS$ 1.2 - 1.2MOQ: 200 Pieces
-
Accessories Connector for Kitchen Cabinet Aluminium Kitchen ProfileUS$ 2.5 - 5MOQ: 0 Ton
-
Building Material Extrusion Profiles_light Box ProfileUS$ 2,500 - 3,500MOQ: 1 Ton
-
Taiwan OEM Aluminum Extrusion Profile Alloy 7000 Series Aluminum AlloyUS$ 2 - 3MOQ: 500 Kilograms
-
OEM LED Extruded Copper HeatsinkUS$ 1 - 10MOQ: 1 Piece
-
Brilliance Extruded Aluminum Heatsink With African PriceUS$ 5 - 20MOQ: 300 Pieces