Help CenterZG42CrMo Steel Castings for Ball Mill
Related Products
-
GS52 Rudder Carrier for 2000TEU Contianer VesselUS$ 2,100 - 2,800MOQ: 10 Metric Tons -
GS52 Rudder Horn for 2000TEU Contianer VesselUS$ 2,100 - 2,800MOQ: 10 Metric Tons
-
GS52 Stern Tube for 2000TEU Contianer VesselUS$ 2,100 - 2,800MOQ: 10 Metric Tons
-
GS52 Bell Mouth for 2000TEU Contianer VesselUS$ 2,100 - 2,800MOQ: 10 Metric Tons
-
Mooring Chock by Steel CastingUS$ 2,100 - 2,800MOQ: 10 Metric Tons
Material:Carbon steel,low alloy steel:ZG20SiMn,ZG50Mn,ZG35SiMn,ZG35CrMo,ZG35SiMnMo,
ZG42CrMo,ZG40Cr,ZG34CrNiMo,ZG40Mn and so on.
Process:Place a pattern in sand to create a mold;
Incorporate a gating system;
Remove the pattern;Fill the mold cavity with molten metal;
Allow the metal to cool;
Break away the sand mold and remove the casting.
Heat treatment.
Chemical composition test,UT/MT test,mechanical property test and so on.
Surface treatment and other requirement from customer.
Standard&certificate:ASTM,BS,NF,DIN,JIS and so on;
ISO 9001:2008;BV,CCS,DNV,NK,RINA,KR and so on.
Weight:from 3 tons to 120 tons per piece
Application:
The products can be widely used in the area of cement mill,rotary kiln,shipbuilding,
metallurgy,mine,sugar mill,powder plant,rail road,engine bed and so on.
We can provide OEM service for cement mill and rotary kiln casting parts,marine steel casting parts,sugar mill machinery parts with carbon steel or low alloy steel.
The casting parts can be supplied as following treatment:
Heat Treatment: Normalized, normalized and tempered,quench and tempered
Machining: Rough machined,semi-finished machined,finished machined
Quality warranty and testing equipment:
Magnetic powder inspection
UT nondestructive test
Dye inspection
Leeb hardness testing equipment
Mechanical property test equipment
Metallographic microscope
Direct-reading spectrometer
Features of our products:
Durable
Excellent tensile strength
Accurate level of tolerance
Good dimensional accuracy
Superb surface finishing
Easy to use and install
Possible defects:
Defect |
Causes |
Unfilled sections |
Insufficient material Low pouring temperature |
Porosity |
Melt temperature is too high Non-uniform cooling rate Sand has low permeability |
Hot tearing |
Non-uniform cooling rate |
Surface projections |
Erosion of sand mold interior A crack in the sand mold Mold halves shift |
There are no these problems for us.
Uniform wall thickness will ensure uniform cooling and reduce defects.
A thick section, often referred to as a hot spot, causes uneven cooling and can result in shrinkage, porosity, or cracking.
Corners
Round corners to reduce stress concentrations and fracture
Inner radius should be at least the thickness of the walls
Machining allowance
Add 0.0625 - 0.25 in. (0.16 - 0.64 mm) to part dimensions to allow for machining to obtain a smooth surface.
Send Inquiry to This Supplier
You May Also Like
-
ANSI 316L Inlet Flange Forged Stainless Steel FlangeUS$ 39MOQ: 1 Piece
-
Custom Hot Forging Parts Carbon Steel & Alloy Steel Forging Service for MachineryNegotiableMOQ: 1 Ton
-
Custom Cut Pure Iron Round Bar With Material Certification and TraceabilityNegotiableMOQ: 50 Kilograms
-
Bolt Hole Plastic Valve and Flange Edge ProtectorNegotiableMOQ: 100 Pieces
-
For Electric Power Fitting Reusable Casting Parts With Machining SurfaceNegotiableMOQ: 100 Pieces
-
High-precision Carbon Steel Flange Customization Large Diameter Stainless Steel Flanging Butt Welding Flange Carbon Steel Flat Welding FlangeUS$ 1.5 - 100MOQ: 1 Piece
-
CNC Machining Parts Ductile Iron Material of Construction Engineering Fittings Parts FastenerUS$ 1 - 2MOQ: 1000 Kilograms
-
Forged Aluminum JointsUS$ 0.1 - 0.1MOQ: 100 Pieces
-
Metal Pipe Flange for 25mm Suqre PipeUS$ 0.6 - 1.5MOQ: 1000 Pieces
-
Cast Iron Manhole Covers Nodular Round Ductile Corrosion Resistance Security High Quality Manhole Covers SizesUS$ 800 - 1,250MOQ: 10 Tons