Heat Insulation Plastic Resin Roofing Material

Name: Heat Insulation Plastic Resin Roofing Material
Brand: JELI
SKU: 115583393

US$ 5.5 - 11 MOQ: 2000 Square Meters

Key Specifications

Place of Origin:

Shandong, China

Brand Name:

JELI

Laizhou Jieli Industrial Co., Ltd.

Payment & Shipping

Payment Methods:

Port of Shipment:

qingdao

Delivery Detail:

Delivery time depends on order quantity.

Place of Origin Shandong, China

Brand Name JELI

Specifications

Excellent weather and corrosion resistance
thermal insulation and sound absorption
light weight and load bearing
color last

Heat Insulation:The coefficient of heat conductivity is 0.325w/m.k. which is 1/3 of clay tile,1/5 of 10-mm-thick cement tile, and 1/2000 of 0.5-mm-thick color coated steel tile.
Light weight: about 6.0kg/sqms.
Color Lasting: E<5 can be guaranteed within 10-15 years in Arizona and Florida, USA.
loading bearing: No damage when 150kg is evenly loaded with the support distance being 750mm.
Stable volume
Corrosion resistance
Good water resistance
Impact resistance and low temperature resistance
Difficult to be burned:B1
Environment friendly and energy saving

Applications of Heat Insulation plastic resin roofing material :

It is suitable for using in roof decoration of all kinds of industrial and civil buildings, such as the roof

of flat-to-sloping projects, high-grade workshops, warehouses, gymnasiums, super markets,

villas, gardens, pavilions, etc.

Technical parameters of Heat Insulation plastic resin roofing material :

Heat-Resistance	(72°c,6h)no deformatio, no viscousness	High-low temperature change	±0.11%
Cold-Resistance	(-40 °c,6h) no crack in suirface	Fire-protection	Class B1 Retardant Building Materials
Bending capability	25mm	Vicat softening temperature	≥75°c
Flexural load	800N, no crack	Water absorption rate	≤0.05%
Fleural strength	72MPa	Nail force	≥46N
Tensile strength	30MPa	Chemical resistance properties	No reaction in salt, alkali(≤60%)
heat conductivity	0.325w/m.k	Expansion coefficient	4.93x10^-5(1/°c)