High Tension Hot Dipped Galvanized Steel Wire Binding Wire

Steel rod coil-wire drawing-wire annealing-rust removing-acid wasting-boiling-drying-zinc feeding-wire coiling

• Wire Rod(low carbon steel, ISQ195, ASTM,SAE 1006/1008)
• Wire Drawing(draw 6.5mm wire to 4.mm or other diameter, two types of drawing methods)
• Annealing(wire go through the high temperature, improve T/S, preparation for the zinc coating)
• Zinc coating(electro GI wire and hot-dipped GI wire, dealed with electro polish and high temperature. More zinc coating, the better resistance of corrosion)
• Wire Coiling(Weight of coil/roll: 200kg, 100kg, 50kg, 25kg, 10kg, 2-8kg)

 Galvanized iron wire is made with mild steel, hard-drawn, and then galvanized. It is rust-resistant, and very versatile in applications. Galvanized iron wire can be supplied in the form of coil wire, spool wire or further processed into straightened cut wire or U type wire.

Annealing is the key determinant of the wire T/S

2.Processing of High Tension Hot Dipped Galvanized Steel Wire Binding Wire

Hot dipped galvanized wire from choiced low carbon steel wire, through the strict process of Wire Drawing---Annealing---Acid Washing---Water Clearing---Drying---Galvanizing--Coiling, in this way, excellent flexibility and tensile strength could be guaranteed. 

3.Technical and Mechanical Characters of High Tension Hot Dipped Galvanized Steel Wire Binding Wire

Material: Q195/235 low carbon iron wire

Wire Diameter: 0.7mm-4.9mm

Zinc Coating: Commercial grade: 30-60grams/sq.m

Heavy coating: >=100grams<=300grams/sq.m

Tensile Strength: 350-550Mpa

Detailed Specifications:

Weight of coil/roll: 200kg, 100kg, 50kg, 25kg, 10kg, 2-8kg

Packaging: Plastic film inside, Hessian or woven bag outside or as require

Inner with plasic film and outside with weaving bags.