Help CenterBitumen Waterproof Membrane Self-adhesive
Related Products
-
Reactive Adhesive Crossing-Laminated Membrane (RAM-CL) 1.5MMUS$ 2.92 - 2.92MOQ: 1000 Square Meters -
Reactive Adhesive Crossing-Laminated Membrane (RAM-CL) 1.2MMUS$ 2.92 - 2.92MOQ: 1000 Square Meters
-
Reactive Adhesive Crossing-Laminated Membrane (RAM-CL) 2.0MMUS$ 2.92 - 2.92MOQ: 1000 Square Meters
-
High Quality Self Adhered Polymer Modified Asphalt Waterproof MembraneUS$ 2 - 5MOQ: 1000 Square Meters
-
Self-adhered Asphalt Basement Waterproof MembraneUS$ 2 - 5MOQ: 1000 Square Meters
Product Description
bitumen adhesive tape/waterproof materials/ building materials
Self Adhesive Waterproof Membrane
Introduction
Hongyuan Waterproof has newly developed RAM-CL, the self-adhesive membrane made from cross laminating HDPE film, asphalt and high polymer adhesive. This product is featured by high property performance, cold application, excellent size stability, anti-UV and good tear resistance.
HDPE film used in this product is manufactured through cross-lamination processing, which enables the film elongation stable both in MD and TD, while no deformation is caused. The polymer (chain) and cement polymer (silicate) function together to form cross interface structure and ensure a permanent, continous seal on cement base.
Proproduct
Product Mechanism
Hongyuan crossing-laminated HDPE filme is made by special formula. It overcomes shortcomings of ordinary film and have high tensile strength, solar stable and no bubbles.
Besides, the longitudinal tensile strength of ordinary HDPE film is larger than its transverse tensile strength. While the longitudinal and transverse value of Hongyuan RAM-CL is equal, which enables the sheet has stronger adhesion on fasteners than ordinary membrane.
An ordinary HDPE film is single directional stretching film, waterproof membrane with this film is easily wrinkled when temperature change, even broken if heavy deformation.
Feature
Excellent physical property
- Superior shank tear strength and watertightness in scres fixed position
- Better adhesion on screws and fasteners than ordinary membrane, stronger tear resistance in both direction.
- Good tensile strength and weatherability
- Size stable and no crease, a reliable safeguard for waterproof
Friendly construction performance
- Firm bonding performance between membrane and base. If any damage on membrane sheet, the leaking water is confined in certain area without channeling. Leakage point is same with broken point, convenient for examining and repaire. Its unique "self-healing" function ensures pin-holes self-healing.
- Good adaptability to construction environment. It can be applied on wet base without use of primer, solvents or fire, which guarantees construction period and avoids environment pollution.
- Apple green facial film eliminates light pollution compared to silver white surface.
- Adaptability to weather change from hot area to cold district, good adhesion in special-shaped part with no empty hollowing.
Application
- RAM-CL membrane is recommended to apply in non-exposed roofs, underground waterproof projects, subways, tunnels and water channels. It is specially used in such constructions that no open fire is allowed to used.
- Cement mortar is used to install RAM-CL onto base, while self-adhesive is recommended to use between membrane sheets.
Specification
Width: 1.0m
Thickness: 1.2mm 1.5mm 2.0mm
Length: 20m
Storage
1. Packing: roll
2. When stored and transported, different type and specification will arranged separately, no disorder.
3. Avoiding sunshine and rain, note ventilation.
4. Store temperature not excess 45ºC, stand on the land will not excess 2 layer.
Technical Data sheet
No. |
Item |
Index |
||||||
Type I |
Type II |
|||||||
1 |
Tensile strength, N/50mm |
≥210 |
≥220 |
|||||
2 |
Breaking elongation, % |
≥160 |
≥200 |
|||||
3 |
Impermeability, (30 Mpa×120min) |
No leakage |
||||||
4 |
Tear resistance, N |
≥25 |
||||||
5 |
Nail-rod tear strength, N |
≥110 |
||||||
6 |
Low temperature flexibility, degree |
No craking under -15 degree |
No craking under -25 degree |
|||||
7 |
Peel strength between sheets, N/mm |
No treatment |
≥1.0 |
|||||
After heating | ||||||||
8 |
Heat resistance, (70degree×2h) |
No slipping, flowing or dripping |
||||||
9 |
Peel strength between sheet and cement mortar, N/mm |
No treatment |
≥2.0 |
|||||
After heating |
≥1.5 |
|||||||
10 |
Peel strength after sheet and mortar soaked in water, N/mm |
≥1.5 |
||||||
11 |
Size stability |
Appearance |
No slipping, flowing or dripping |
|||||
change rate, % |
± 2.0 |
|||||||
12 |
Oil permeability, pieces |
≤2 |
||||||
13 |
Holding Power, min |
≥15 |
||||||
14 |
Artificial weathering test |
Appearance |
No slipping, flowing or dripping |
|||||
Pull retention, % |
≥80 |
|||||||
Low temperature flexibility |
No craking under -13 degree |
|||||||
|
|
|
|
|
|
|||
|
|
|
||||||
|
|
|||||||
15 |
Heat aging test (70degree×168h) |
Pull retention, % |
≥90 |
|||||
Breaking elongation retention, % |
≥80 |
|||||||
Low temperature flexibility |
No craking under -13 degree |
|||||||
16 |
Salt treatment a (20% NaCl solution×30d ) |
Pull retention, % |
≥90 |
|||||
Elongation retention, % |
≥80 |
|||||||
Low temperature flexibility |
No craking under -13 degree |
|||||||
17 |
Alkali treatment a (saturated NaOH solution×30d)) |
Pull retention, % |
≥90 |
|||||
Elongation retention, % |
≥80 |
|||||||
Low temperature flexibility |
No craking under -13 degree |
|||||||
18 |
Chlorideion penetration resistance, mg/cm 2 d |
≤5.0x10 -3 |
||||||
Note: a for special designed projects that require these testing items | ||||||||
Send Inquiry to This Supplier
You May Also Like
-
High Adhesive, Water-proof, Anti Corrosion, Weather-resistant Self-adhesive Bitumen MembraneNegotiableMOQ: 100 Rolls
-
1.5mm Thick UV-resistant Geomembrane High Strength Waterproof Membrane for Dam and Canal Lining BOLIUS$ 0.15 - 0.20MOQ: 10 Square Meters
-
GeomembraneNegotiableMOQ: 2700 Rolls
-
Non-curable Rubber Paint Rubber Asphalt Waterproof Coating Made in ChinaUS$ 1.5 - 6MOQ: 500 Kilograms
-
Low Cost Waterproof Material ManufactureUS$ 1,000 - 50,000MOQ: 1 Set
-
PTFE Architectural Membrane MaterialNegotiableMOQ: 1
-
Special Compound BaseUS$ 0.12 - 0.25MOQ: 7000 Square Meters
-
PolyLock/HDPE Lock/ E Lock/ HDPE E Lock/Geomembrane Attaches HDPE GeomembranesUS$ 10 - 50MOQ: 1 Piece
-
Breathable House Wrap Membrane Roofing Waterproofing MembraneUS$ 0.42 - 0.42MOQ: 5000 Square Meters
-
<MIicroVENT> Waterproof Vent MembraneUS$ 0.1 - 3MOQ: 10000 Pieces