Wraparound Heat Shrinkable Corrosion Protection Sleeve For Pipeline Weld Joints

Specifications

Wraparound Heat Shrinkable
Corrosion Protection Sleeve
For Pipeline Weld Joints
Over 10 years expriences.
Anticorrosion

Wraparound Heat Shrinkable Corrosion Protection Sleeve For Pipeline Weld Joints

 

1.1  Product Structure                                                        

• The inner layer is two-components epoxy primer which coated on steel pipe;
• Intermediate level is special hot melt adhesive;
• Outer layer is modified radiation crossing linking polyethylene backing.

 1.2  Features & Benefits:                                                

 

Heat Shrinkable Sleeves provide great corrosion protection, Superior resistance to Cathodic Disbondment and excellent durability against abrasion and chemical attack. The result is effective, good performance of sealing, wide application, easy to operate and preheating temperature low (50 °C) ,long term protection against corrosion.

• Cross-linked backing provides superior abrasion, mechanical and chemical attack resistance.
• High performance adhesive provides excellent resistance to Cathodic   Disbondment to ensure long-term corrosion protection.
• Just-in-time customized lengths allow bulk rolls to be field cut to protect any pipe size
• Open sleeve configuration allows the product to be applied after the pipeline has been welded and cleaned.

1.3  Specification( mm)                                                  

 

Pipeline size: from Ø 108 to Ø 1554 ( 4’’---60’’)

Sleeves width: 100mm, 150mm,200mm, 300mm,450mm,500mm,600mm,900mm

Closure patch: 100mm, 150mm,200mm (4’’, 6’’, 8’’)

 

Model:  HSS 3600/505/ Ø 1066.8

 

     HSS--Heat shrinkable sleeves

     3600------Roll length(mm)

     505----- -Roll Width (as supplied)

     Ø 1066.8----Joint or pipeline Diameter

 

1.4   Technical Datas

 

Width deviation (max)	±10% width or 0.25 in.(6mm),	AWWAC216-5.3.1
Dielectric strength	400 V/mil(15 V/um)	ASTM D149
Volume resistivity	1014 ohm-cm	ASTM D257
Adhesion to steel	15 lb/in.width (25 N/cm)	ASTM D1000
Lap shear	12 psi	ASTM D1002
Heat shock	No visual cracking,flowing, or dripping	AWWAC216-5.3.8
Tensile strength	2200 psi min	ASTM D638
Elongation 23	400% min	ASTM D638
Impact resistance	25 in.-lb(282cm-N)	ASTM G14
Impact Resistance	ASTM G14	≥50
Cathodic Disbondment at 23°C 30 days mm rad	ASTM G 8	≤25
Dielectric Breakdown Voltage 23°C MV/M	ASTM D 149	≥15