Specifications

weather resistance steel and special gas shielding welding wires YC-YL457(Q)   

This flux cored wire is specially used for welding transfer bridge,such as PD3 steel and U71Mn steel

YC-YL457(Q)  was developed for out-of-position welding. This flux cored wire
will deposit out-of-position welds at substantially higher welding currents than other stainless steel flux cored wires, resulting in a higher deposition rate. The slag is selfpeeling and minimizes cleanup.

YC-YL457(Q)   was formulated for use with 75% Argon/25% CO² shielding gas; however, straight CO² may also be used. The 75/25 mixture will produce a smooth arc with virtually no spatter and slightly higher yield and tensile strengths than CO². The mechanical properties and deposit analysis
will meet AWS 5.22 specifications with either gas.

Packing:

spool+carton+pallet

One spool is vacuum packed by aluminum film and then one carton 

Mechanical Properties of Deposited Metal:

TensileStrength:590MPA,Elongation:36%

  Chemical Composition of deposited metal

 Size and Recommended Current (DC-) and Voltage Range

  Procedures may vary with change in position, base metals, filler metals,equipment and other changes.

Shielding Gas: CO2 or70% Ar+CO2

Stainless steel flux-cored wires  

 YC-YL457(Q) 

Available Diameters:

1.0mm/1.2mm / 1.6mm 

Shielding Gas:CO2 or75% Ar+CO2

Stainless steel flux-cored wire 
a.all position capability 
b.Low fume&spatter. 
c.good slag removabilty 
d.less operater skill